| Grivory XE 3903 natural is a 50% glass-fibre reinforced flame retardant (UL 94 V-0) engineering thermoplastic material based on a semi-crystalline, partially aromatic copolyamide. Grivory XE 3903 natural is halogen free and free of red phosphorous, the material has a light natural colour. RoHS:Grivory XE 3903 natural is in compliance with RoHS (2002/95/EC, Restriction of Hazardous Substances) WEEE:Parts produced from Grivory XE 3903 natural are not subject to "selective treatment" according to the Directive 2002/96/EC on Waste Electrical and Electronic Equipment. |
| Density | 1.65g/cc | 0.0596lb/in | *** 1183 |
| Moisture Absorption at Equilibrium | 1.0 % @Temperature 23.0 °C | 1.0 % @Temperature 73.4 °F | 50% R.H.; *** 62 |
| Water Absorption at Saturation | 3.0 % @Temperature 23.0 °C | 3.0 % @Temperature 73.4 °F | *** 62 |
| Linear Mold Shrinkage | 0.00050cm/cm | 0.00050in/in | *** 294 |
| Linear Mold Shrinkage, Transverse | 0.0060cm/cm | 0.0060in/in | *** 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 275MPa | 39900psi | *** 2039-1 |
| Tensile Strength at Break | 155MPa | 22500psi | 5mm/min; *** 527 |
| Elongation at Break | 1.5 % | 1.5 % | 5mm/min; *** 527 |
| Tensile Modulus | 17.0GPa | 2470ksi | 1 mm/min; *** 527 |
| Charpy Impact Unnotched | 4.00J/cm @Temperature -30.0 °C | 19.0ft-lb/in @Temperature -22.0 °F | *** 179/2-1eU |
| 4.50J/cm @Temperature 23.0 °C | 21.4ft-lb/in @Temperature 73.4 °F | *** 179/2-1eU | |
| Charpy Impact, Notched | 1.00J/cm @Temperature 23.0 °C | 4.76ft-lb/in @Temperature 73.4 °F | *** 179/2-1eA |
| 1.00J/cm @Temperature -30.0 °C | 4.76ft-lb/in @Temperature -22.0 °F | *** 179/2-1eA | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+12ohm-cm | 1.00e+12ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+11ohm | 1.00e+11ohm | IEC 60093 |
| Dielectric Strength | 42.0kV/mm | 1070kV/in | IEC 60243-1 |
| Comparative Tracking Index | 600V | 600V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 310°C | 590°F | DSC; *** 11357 |
| Flammability, UL94 | V-0 @Thickness 0.350 - 3.20 mm | V-0 @Thickness 0.0138 - 0.126 in | *** 1210 |
改性PPA塑料的热变形温度高达300℃以上，连续使用温度可达170℃，能满足您所需的短期和长期的热性能。它可在宽广的温度范围内和高湿度环境中保持其优越的机械性特性—强度、硬度、耐疲劳性及抗蠕变性。增韧吕级PPA结合优越的韧度与一定范围的硬度和柔性，在扣件中要求一次性使用的刚性、以及重复性使用中挠屈性的良好选择。同时提供特殊品级的产品应用于可喷涂和可电镀的表面，防火性性要求的应用