代理美国杜邦耐水解PPA Zytel HTN 51G35HSLR
Density | 1.47 | -- | g/cm | *** 1183 |
Molding Shrinkage | *** 294-4 | |||
Across Flow | 0.60 | -- | % | |
Flow | 0.20 | -- | % | |
Water Absorption | *** 62 | |||
Saturation, 23°C, 2.00 mm | 4.0 | -- | % | |
Equilibrium, 23°C, 2.00 mm, 50% RH | 1.7 | -- | % | |
Hardness | Dry | Conditioned | Unit | Test Method |
Ball Indentation Hardness(H 961/30) | 310 | -- | MPa | *** 2039-1 |
Mechanical | Dry | Conditioned | Unit | Test Method |
Tensile Modulus | 12000 | 12000 | MPa | *** 527-2 |
Tensile Stress(Break) | 200 | 190 | MPa | *** 527-2 |
Tensile Strain(Break) | 2.3 | 2.0 | % | *** 527-2 |
Flexural Modulus | 10500 | -- | MPa | *** 178 |
Poisson's Ratio | 0.33 | 0.33 | ||
Impact | Dry | Conditioned | Unit | Test Method |
Charpy Notched Impact Strength(23°C) | 9.0 | 8.0 | kJ/m | *** 179/1eA |
Charpy Unnotched Impact Strength(23°C) | 50 | 40 | kJ/m | *** 179/1eU |
Thermal | Dry | Conditioned | Unit | Test Method |
Heat Deflection Temperature | ||||
0.45 MPa, Unannealed | 276 | -- | °C | *** 75-2/B |
1.8 MPa, Unannealed | 262 | -- | °C | *** 75-2/A |
Glass Transition Temperature2 | 135 | 95.0 | °C | *** 11357-2 |
Melting Temperature3 | 300 | -- | °C | *** 11357-3 |
CLTE | *** 11359-2 | |||
Flow | 2.0E-5 | -- | cm/cm/°C | |
Flow : -40 to 23°C | 2.0E-5 | -- | cm/cm/°C | |
Transverse | 5.8E-5 | -- | cm/cm/°C | |
Transverse : -40 to 23°C | 5.5E-5 | -- | cm/cm/°C |