NORYL GTX985 is a 18% mineral filled material. This material combines high stiffness and excellent temperature resistance with conductivity for electrostatic painting.
Density / Specific Gravity | 1.25 | g/cm | ASTM D792,*** 1183 |
Melt Mass-Flow Rate (MFR)(280°C/5.0 kg) | 16 | g/10 min | ASTM D1238 |
Melt Volume-Flow Rate (MVR)(280°C/5.0 kg) | 15 | cm/10min | *** 1133 |
Molding Shrinkage - Flow(3.20 mm) | 1.1 | % | Internal Method |
Water Absorption(Equilibrium, 23°C, 50% RH) | 1.1 | % | *** 62 |
Charpy Notched Impact Strength6(23°C) | 4.0 | kJ/m | *** 179/1eA |
Notched Izod Impact | |||
-30°C | 40 | J/m | ASTM D256 |
23°C | 45 | J/m | ASTM D256 |
-30°C7 | 4.0 | kJ/m | *** 180/1A |
23°C7 | 4.0 | kJ/m | *** 180/1A |
Unnotched Izod Impact Strength8 | *** 180/1U | ||
-30°C | 55 | kJ/m | |
23°C | 60 | kJ/m | |
Instrumented Dart Impact(23°C, Total Energy) | 10.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load | |||
0.45 MPa, Unannealed, 3.20 mm | 200 | °C | ASTM D648 |
0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span7 | 205 | °C | *** 75-2/Bf |
PPO阻燃性良好，具有自息性，与HIPS混合后具有中等可燃性。质轻，***可用于食品和***行业。耐光性差，长时间在阳光下使用会变色。
6、PPO可以与ABS,HDPE,PPS,PA,HIPS、玻璃纤维等进行共混改性处理。PPO塑胶原料特性A、PPO塑胶原料***、透明、相对密度小，具有优良的机械强度、耐应力松弛、耐蠕变性、耐热性、耐水性、耐水蒸汽性、尺寸稳定性。B、在很宽温度、频变范围内电性能好，不水解、成型收缩率小，难燃有自熄性，耐无机酸、碱、耐芳香烃、卤代烃、油类等性能差，易溶胀或应力开裂。C、它具有刚性大、耐热性高、难燃、强度较高电性能优良等优点。D、PPO还具有***、***、耐污染等优点。E、PPO塑胶原料的介电常数和介电损耗在工程塑料中是***小的品种之一，几乎不受温度、湿度的影响，可用于低、中、高频电场领域。F、PPO的负荷变形温度可达190℃以上，脆化温度为-170℃。 G、主要缺点是熔融流动性差，加工成型困难。