耐化学PPE/PA NORYL GTX902
¥46.50
抗冲击PPE/PA NORYL GTX909
¥46.50
高强度PPE/PA NORYL GTX910
¥46.50
抗冲耐化学PPE/PA NORYL GTX914
¥46.50
***PPE/PA NORYL GTX918W
¥46.50
***流动PPE/PA NORYL GTX918WR
¥46.50
***美国SABIC导电高流动PPE/PA NORYL GTX8720
| 比重 | 1.26 g/cc | 1.26 g/cc | ASTM D792 |
| 密度 | 1.26 g/cc | 0.0455 lb/in | ISO 1183 |
| 水分吸收 | 0.500 % | 0.500 % | 23°C / 50% RH; ISO 62 |
| 饱和吸水率 | 4.0 % | 4.0 % | ISO 62 |
| 线性成型收缩率,Flow | 0.0026 - 0.0030 cm/cm @Thickness 3.20 mm | 0.0026 - 0.0030 in/in @Thickness 0.126 in | SABIC Method |
| 线性成型收缩率，横向 | 0.0072 - 0.0085 cm/cm @Thickness 3.20 mm | 0.0072 - 0.0085 in/in @Thickness 0.126 in | SABIC Method |
| 熔体流动速率 | 8.6 g/10 min @Load 5.00 kg, Temperature 280 °C | 8.6 g/10 min @Load 11.0 lb, Temperature 536 °F | ASTM D1238 |
| 弯曲模量 | 6.60 GPa | 957 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 6.60 GPa | 957 ksi | 2 mm/min; ISO 178 | |
| 悬壁梁缺口冲击强度 | 0.850 J/cm | 1.59 ft-lb/in | ASTM D256 |
| 0.600 J/cm @Temperature -30.0 °C | 1.12 ft-lb/in @Temperature -22.0 °F | ASTM D256 | |
| 10.0 kJ/m | 4.76 ft-lb/in | 80*10*4; ISO 180/1A | |
| 8.00 kJ/m @Temperature -30.0 °C | 3.81 ft-lb/in @Temperature -22.0 °F | 80*10*4; ISO 180/1A | |
| 简支梁缺口冲击强度 | 1.10 J/cm | 5.23 ft-lb/in | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 落锤总能量 | 17.0 J @Temperature 23.0 °C | 12.5 ft-lb @Temperature 73.4 °F | ASTM D3763 |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 体积电阻率 | 1000 - 10000 ohm-cm | 1000 - 10000 ohm-cm | SABIC Method |