Density / Specific Gravity | 1.13 | ASTM D792 | |
Molding Shrinkage - Flow(0.126 in) | 1.3 to 1.7 | % | Internal Method |
Water Absorption | ASTM D570 | ||
24 hr | 0.54 | % | |
Equilibrium, 73°F | 4.4 | % |
Mechanical | Nominal Value | Unit | Test Method |
Tensile Strength1 | ASTM D638 | ||
Yield | 9570 | psi | |
Break | 8560 | psi | |
Tensile Elongation1 | ASTM D638 | ||
Yield | 9.0 | % | |
Break | 50 | % | |
Flexural Modulus2(3.94 in Span) | 344000 | psi | ASTM D790 |
Flexural Strength2(Yield, 3.94 in Span) | 14400 | psi | ASTM D790 |
Impact | Nominal Value | Unit | Test Method |
Notched Izod Impact | ASTM D256 | ||
-22°F | 2.0 | ft·lb/in | |
73°F | 3.3 | ft·lb/in | |
Instrumented Dart Impact | ASTM D3763 | ||
-22°F, Energy at Peak | 212 | in·lb | |
73°F, Energy at Peak | 354 | in·lb |
Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load | ASTM D648 | ||
66 psi, Unannealed, 0.252 in | 399 | °F | |
264 psi, Unannealed, 0.252 in | 257 | °F | |
Vicat Softening Temperature | 473 | °F | ASTM D15253 |