代理美国SABIC抗紫外线PPE/PP NORYL PPX7200U
Density / Specific Gravity | |||
-- | 0.988 | g/cm | ASTM D792 |
-- | 0.990 | g/cm | ISO 1183 |
Melt Mass-Flow Rate (MFR)(260°C/5.0 kg) | 16 | g/10 min | ASTM D1238 |
Melt Volume-Flow Rate (MVR)(260°C/5.0 kg) | 18 | cm/10min | ISO 1133 |
Molding Shrinkage | Internal Method | ||
Flow2 | 0.60 to 0.80 | % | |
Across Flow : 3.20 mm | 0.60 to 0.80 | % | |
Flow : 3.20 mm | 0.60 to 0.80 | % |
Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus | |||
--3 | 1240 | MPa | ASTM D638 |
-- | 1670 | MPa | ISO 527-2/1 |
Charpy Notched Impact Strength8 | ISO 179/1eA | ||
-30°C | 6.0 | kJ/m | |
23°C | 12 | kJ/m | |
Charpy Unnotched Impact Strength8 | ISO 179/1eU | ||
-30°C | 80 | kJ/m | |
23°C | No Break |