***法国阿科玛低烟***PVDF Kynar 3120-15
Density | 1.78 | g/cm | ISO 1183 |
Melt Volume-Flow Rate (MVR)(232°C/3.8 kg) | 4.0 | cm/10min | ISO 1133 |
Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus | 700 | MPa | ISO 527-2 |
Tensile Stress(Yield) | 27.0 | MPa | ISO 527-2 |
Tensile Strain(Yield) | 15 | % | ISO 527-2 |
Nominal Tensile Strain at Break | > 50 | % | ISO 527-2 |
Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength(23°C) | No Break | ISO 179/1eA |
Thermal | Nominal Value | Unit | Test Method |
Heat Deflection Temperature | |||
0.45 MPa, Unannealed | 65.0 | °C | ISO 75-2/B |
1.8 MPa, Unannealed | 48.0 | °C | ISO 75-2/A |
Glass Transition Temperature3 | -36.0 | °C | ISO 11357-2 |
Melting Temperature3 | 164 | °C | ISO 11357-3 |
Electrical | Nominal Value | Unit | Test Method |
Volume Resistivity | 2.0E+14 | ohms·cm | IEC 60093 |
Relative Permittivity(100 Hz) | 6.70 | IEC 60250 | |
Dissipation Factor(100 Hz) | 0.11 | IEC 60250 |