| 比重 | 1.24 | g/cm | ASTM D792, *** 1183 |
| 熔流率（熔体流动速率）(280°C/5.0 kg) | 16 | g/10 min | ASTM D1238 |
| 溶化体积流率（MVR）(220°C/5.0 kg) | 14.0 | cm/10min | *** 1133 |
| 收缩率 - 流动(3.20 mm) | 0.70 到 0.90 | % | 内部方法 |
| 吸水率 | *** 62 | ||
| 饱和, 23°C | 3.6 | % | *** 62 |
| 平衡, 23°C, 50% RH | 0.70 | % | *** 62 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸模量 | |||
| --1 | 4450 | MPa | ASTM D638 |
| -- | 4790 | MPa | *** 527-2/1 |
| 抗张强度 | |||
| 屈服2 | 64.0 | MPa | ASTM D638 |
| 屈服 | 61.0 | MPa | *** 527-2/5 |
| 断裂3 | 62.0 | MPa | ASTM D638 |
| 断裂 | 61.0 | MPa | *** 527-2/5 |
| 简支梁缺口冲击强度9(23°C) | 3.8 | kJ/m | *** 179/1eA |
| 悬壁梁缺口冲击强度 | |||
| -30°C | 31 | J/m | ASTM D256 |
| 23°C | 39 | J/m | ASTM D256 |
| -30°C10 | 3.5 | kJ/m | *** 180/1A |
| 23°C11 | 4.2 | kJ/m | *** 180/1A |
| 装有测量仪表的落镖冲击(23°C, Total Energy) | 7.00 | J | ASTM D3763 |