Density | 1.29 | g/cm | ISO 1183 |
Molding Shrinkage2 | ISO 294-4 | ||
Across Flow : 2.00 mm | 0.40 to 0.60 | % | |
Flow : 2.00 mm | 0.40 to 0.60 | % | |
Water Absorption(24 hr, 23°C) | 0.030 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus | ISO 527-1/1 | ||
23°C | 7790 | MPa | |
60°C | 6890 | MPa | |
91°C | 6000 | MPa | |
121°C | 4270 | MPa |
Charpy Notched Impact Strength | ISO 179/1eA | ||
-20°C | 5.9 | kJ/m | |
23°C | 6.9 | kJ/m | |
Charpy Unnotched Impact Strength | ISO 179/1eU | ||
-20°C | 25 | kJ/m | |
23°C | 25 | kJ/m |
| Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load | |||
0.45 MPa, Unannealed | 140 | °C | ISO 75-2/B |
1.8 MPa, Unannealed | 130 | °C | ISO 75-2/A |
Continuous Use Temperature3 | 120 | °C | ASTM E1641/E1877 |
Vicat Softening Temperature | 140 | °C | ISO 306/B50 |
CLTE - Flow(30 to 100°C) | 2.5E-5 | cm/cm/°C | ISO 11359-2 |