| Density | 1.90g/cc | 0.0686lb/in | *** 1183 |
| Water Absorption at Saturation | 0.020 % | 0.020 % | *** 62 |
| Linear Mold Shrinkage, Flow | 0.0020-0.0060cm/cm | 0.0020-0.0060in/in | *** 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0030-0.0070cm/cm | 0.0030-0.0070in/in | *** 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 100 | 100 | *** 2039-2 |
| Tensile Strength at Break | 145MPa | 21000psi | 5mm/min; *** 527-2/1A |
| Elongation at Break | 1.0 % | 1.0 % | 5mm/min; *** 527-2/1A |
| Tensile Modulus | 17.3GPa | 2510ksi | 1mm/min; *** 527-2/1A |
| Flexural Strength | 220MPa | 31900psi | *** 178 |
| Flexural Modulus | 16.7GPa | 2420ksi | *** 178 |
| Izod Impact, Notched (***) | 7.00kJ/m | 3.33ft-lb/in | *** 180/1A |
| 7.00kJ/m @Temperature 30.0 °C | 3.33ft-lb/in @Temperature 86.0 °F | *** 180/1A | |
| Charpy Impact Unnotched | 2.70J/cm | 12.8ft-lb/in | *** 179/1eU |
| 2.70J/cm @Temperature -30.0 °C | 12.8ft-lb/in @Temperature -22.0 °F | *** 179/1eU | |
| Charpy Impact, Notched | 0.700J/cm | 3.33ft-lb/in | *** 179/1eA |
| 0.700J/cm @Temperature -30.0 °C | 3.33ft-lb/in @Temperature -22.0 °F | *** 179/1eA | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | >=1.00e+13ohm-cm | >=1.00e+13ohm-cm | IEC 60093 |
| Surface Resistance | >=1.00e+15ohm | >=1.00e+15ohm | IEC 60093 |
| Dielectric Constant | 4.9 @Frequency 10000 Hz | 4.9 @Frequency 10000 Hz | IEC 60250 |
| 4.9 @Frequency 1.00e+6 Hz | 4.9 @Frequency 1.00e+6 Hz | IEC 60250 | |
| Dielectric Strength | 26.0kV/mm | 660kV/in | IEC 60243-1 |
| Dissipation Factor | 0.00050 @Frequency 1000 Hz | 0.00050 @Frequency 1000 Hz | IEC 60250 |
| 0.0010 @Frequency 1.00e+6 Hz | 0.0010 @Frequency 1.00e+6 Hz | IEC 60250 | |
| Comparative Tracking Index | 175V | 175V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 280°C | 536°F | *** 11357-1,-2,-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 270°C | 518°F | *** 75-1, -2 |
| Deflection Temperature at 8.0 MPa | 220°C | 428°F | *** 75-1, -2 |
| Glass Transition Temp, Tg | 90.0°C | 194°F | *** 11357-1,-2,-3 |
| Flammability, UL94 | V-0 @Thickness 0.810 mm | V-0 @Thickness 0.0319 in | |
| V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | ||