耐候40%玻纤PPS Torelina AR04
¥55.50
耐湿热30%玻纤PPS Torelina A673M-T
¥55.50
40%GF增韧PPS Torelina A674M2
¥55.50
65%玻矿PPS Torelina A310MX04
¥55.50
70%玻矿低翘曲PPS Torelina A310M
¥55.50
原包深圳东丽高流动低飞边PPS Torelina A604-X95
Density(23°C) | 1.66 | g/cm | *** 1183 |
Molding Shrinkage2 | Internal Method | ||
Across Flow : 3.00 mm | 0.80 | % | |
Flow : 3.00 mm | 0.20 | % | |
Water Absorption(24 hr, 23°C) | 0.020 | % | *** 62 |
| Hardness | Nominal Value | Unit | Test Method |
Rockwell Hardness(R-Scale) | 122 | *** 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Stress(23°C) | 190 | MPa | *** 527-2 |
Tensile Strain(Break, 23°C) | 1.7 | % | *** 527-2 |
Flexural Modulus(23°C) | 15000 | MPa | *** 178 |
Flexural Stress(23°C) | 290 | MPa | *** 178 |
Shear Strength(23°C) | 75.0 | MPa | JIS K7214 |
Coefficient of Friction3 | 0.25 | ||
Taber Abrasion Resistance(1000 Cycles) | 50.0 | mg | *** 9352 |
| Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength(23°C) | 11 | kJ/m | *** 179 |
Charpy Unnotched Impact Strength(23°C) | 45 | kJ/m | *** 179 |
| Thermal | Nominal Value | Unit | Test Method |
Heat Deflection Temperature(1.8 MPa, Unannealed) | 260 | °C | *** 75-2/A |
Melting Temperature | 278 | °C | *** 11357-3 |
CLTE | *** 11359-2 | ||
Flow | 2.3E-5 | cm/cm/°C | |
Transverse | 3.5E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
Volume Resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
Electric Strength | 25 | kV/mm | IEC 60243-1 |
Dielectric Constant4(23°C, 1 MHz) | 3.60 | IEC 60250 | |
Dissipation Factor4(23°C, 1 MHz) | 2.0E-3 | IEC 60250 | |
| Flammability | Nominal Value | Unit | Test Method |
Flame Rating(0.200 mm) | V-0 | UL 94 |