经销德国巴斯夫PSU Ultrason S3010增韧高抗冲抗化学PSU
Density | 1.23 | g/cm | ISO 1183 |
Melt Volume-Flow Rate (MVR)(360°C/10.0 kg) | 40 | cm/10min | ISO 1133 |
Molding Shrinkage | ISO 294-4 | ||
Across Flow | 0.74 | % | |
Flow | 0.70 | % | |
Water Absorption | ISO 62 | ||
Saturation, 23°C | 0.80 | % | |
Equilibrium, 23°C, 50% RH | 0.30 | % | |
Hardness | Nominal Value | Unit | Test Method |
Ball Indentation Hardness | 135 | MPa | ISO 2039-1 |
Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus(23°C) | 2550 | MPa | ISO 527-1 |
Tensile Stress(Yield, 23°C) | 75.0 | MPa | ISO 527-2 |
Tensile Strain(Yield, 23°C) | 6.0 | % | ISO 527-2 |
Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength | ISO 179 | ||
-30°C | 6.0 | kJ/m | |
23°C | 5.5 | kJ/m | |
Charpy Unnotched Impact Strength | ISO 179 | ||
-30°C | No Break | ||
23°C | No Break | ||
Notched Izod Impact Strength | ISO 180 | ||
-30°C | 6.0 | kJ/m | |
23°C | 5.5 | kJ/m |
Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load(1.8 MPa, Unannealed) | 177 | °C | ISO 75-2/A |
CLTE - Flow | 5.3E-5 | cm/cm/°C | |
RTI Elec | UL 746B | ||
1.6 mm | 155 | °C | |
3.0 mm | 155 | °C | |
RTI Imp | UL 746B | ||
1.6 mm | 130 | °C | |
3.0 mm | 130 | °C | |
RTI Str | UL 746B | ||
1.6 mm | 155 | °C | |
3.0 mm | 155 | °C |
Electrical | Nominal Value | Unit | Test Method |
Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
Electric Strength | 37 | kV/mm | IEC 60243-1 |
Dielectric Constant | IEC 60250 | ||
100 Hz | 3.10 | ||
1 MHz | 3.10 | ||
Dissipation Factor | IEC 60250 | ||
100 Hz | 8.0E-4 | ||
1 MHz | 6.4E-3 | ||
Comparative Tracking Index | 125 | V | IEC 60112 |
Flammability | Nominal Value | Unit | Test Method |
Flame Rating | UL 94 | ||
1.6 mm | HB |