LNP THERMOCOMP D351 玻璃纤维、阻燃剂
¥98.00
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
---|---|---|---|---|
FLAME CHARACTERISTICS | 1) | |||
UL Yellow Card Link | E207780-103127360 | - | - | |
UL Recognized, 94V-0 Flame Class Rating | ≥0.6 | mm | UL 94 | |
UL Recognized, 94V-1 Flame Class Rating | ≥0.5 | mm | UL 94 | |
Glow Wire Ignitability Temperature, 2.0 mm | 850 | °C | IEC 60695-2-13 | |
Glow Wire Ignitability Temperature, 1.0 mm | 850 | °C | IEC 60695-2-13 | |
Glow Wire Ignitability Temperature, 1.6 mm | 850 | °C | IEC 60695-2-13 | |
Glow Wire Flammability Index, 2.0 mm | 960 | °C | IEC 60695-2-12 | |
Glow Wire Flammability Index, 1.0 mm | 960 | °C | IEC 60695-2-12 | |
Glow Wire Flammability Index, 1.6 mm | 960 | °C | IEC 60695-2-12 | |
MECHANICAL | 2) | |||
Flexural Modulus, 1.3 mm/min, 50 mm span | 6050 | MPa | ASTM D790 | |
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 161 | MPa | ASTM D790 | |
Flexural Stress, brk, 1.3 mm/min, 50 mm span | 158 | MPa | ASTM D790 | |
Flexural Modulus, 2 mm/min | 6150 | MPa | ISO 178 | |
Flexural Stress, yield, 2 mm/min | 161 | MPa | ISO 178 | |
Flexural Stress, break, 2 mm/min | 160 | MPa | ISO 178 | |
Tensile Modulus, 5 mm/min | 6700 | MPa | ASTM D638 | |
Tensile Stress, brk, Type I, 5 mm/min | 109 | MPa | ASTM D638 | |
Tensile Strain, brk, Type I, 5 mm/min | 2.6 | % | ASTM D638 | |
Tensile Modulus, 1 mm/min | 6650 | MPa | ISO 527 | |
Tensile Stress, break, 5 mm/min | 107 | MPa | ISO 527 | |
Tensile Strain, break, 5 mm/min | 2.6 | % | ISO 527 | |
IMPACT | 2) | |||
Izod Impact, notched, 23°C | 140 | J/m | ASTM D256 | |
Izod Impact, notched, -30°C | 90 | J/m | ASTM D256 | |
Izod Impact, unnotched, 23°C | 680 | J/m | ASTM D4812 | |
Izod Impact, notched 80*10*4 +23°C | 13 | kJ/m² | ISO 180/1A | |
Izod Impact, notched 80*10*4 -30°C | 9 | kJ/m² | ISO 180/1A | |
Izod Impact, unnotched 80*10*4 +23°C | 41 | kJ/m² | ISO 180/1U | |
Instrumented Dart Impact Total Energy, 23°C | 22 | J | ASTM D3763 | |
THERMAL | 2) | |||
HDT, 1.82 MPa, 3.2mm, unannealed | 115 | °C | ASTM D648 | |
HDT, 0.45 MPa, 3.2 mm, unannealed | 120 | °C | ASTM D648 | |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 116 | °C | ISO 75/Af | |
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 121 | °C | ISO 75/Bf | |
Vicat Softening Temp, Rate B/50 | 122 | °C | ISO 306 | |
Vicat Softening Temp, Rate B/120 | 125 | °C | ISO 306 | |
CTE, 23°C to 80°C, flow | 2.6E-05 | 1/°C | ASTM E831 | |
CTE, 23°C to 80°C, xflow | 7.5E-05 | 1/°C | ASTM E831 | |
CTE, -40°C to 40°C, flow | 2.5E-05 | 1/°C | ASTM E831 | |
CTE, -40°C to 40°C, xflow | 6.3E-05 | 1/°C | ASTM E831 | |
Relative Temp Index, Elec | 1) | 80 | °C | UL 746B |
Relative Temp Index, Mech w/impact | 1) | 80 | °C | UL 746B |
Relative Temp Index, Mech w/o impact | 1) | 80 | °C | UL 746B |
PHYSICAL | 2) | |||
Density | 1.35 | g/cm³ | ASTM D792 | |
Melt Flow Rate, 300°C/2.16 kgf | 25 | g/10 min | ASTM D1238 | |
Melt Flow Rate, 300°C/1.2 kgf | 12 | g/10 min | ASTM D1238 | |
Melt Volume Rate, MVR at 300°C/2.16 kg | 21 | cm³/10 min | ISO 1133 | |
Melt Volume Rate, MVR at 300°C/1.2 kg | 10 | cm³/10 min | ISO 1133 | |
Mold Shrinkage, flow, 24 hrs | 4) | 0.2-0.4 | % | ASTM D955 |
Mold Shrinkage, xflow, 24 hrs | 4) | 0.2-0.4 | % | ASTM D955 |
Water Absorption, (23°C/24hrs) | 0.03 | % | ISO 62-1 | |
ELECTRICAL | 2) | |||
Dielectric Constant, 1.1 GHz | 3.25 | - | SABIC method | |
Dielectric Constant, 1.9 GHz | 3.26 | - | SABIC method | |
Dielectric Constant, 5 GHz | 3.26 | - | SABIC method | |
Dielectric Constant, 10 GHz | 3.26 | - | SABIC method | |
Dissipation Factor, 1.1 GHz | 0.0068 | - | SABIC method | |
Dissipation Factor, 1.9 GHz | 0.0069 | - | SABIC method | |
Dissipation Factor, 5 GHz | 0.0071 | - | SABIC method | |
Dissipation Factor, 10 GHz | 0.0073 | - | SABIC method | |
Surface Resistivity | >1.0E+16 | Ω | ASTM D257 | |
Volume Resistivity | >1.0E+16 | Ω.cm | ASTM D257 | |
Comparative Tracking Index (UL) {PLC} | 3 | PLC Code | UL 746A | |
INJECTION MOLDING | 3) | |||
Drying Temperature | 110 | °C | ||
Drying Time | 3-6 | Hrs | ||
Maximum Moisture Content | 0.02 | % | ||
Melt Temperature | 285-310 | °C | ||
Nozzle Temperature | 285-305 | °C | ||
Front - Zone 3 Temperature | 280-300 | °C | ||
Middle - Zone 2 Temperature | 270-290 | °C | ||
Rear - Zone 1 Temperature | 260-280 | °C | ||
Mold Temperature | 80-110 | °C | ||
Back Pressure | 0.1-0.3 | MPa | ||
Screw Speed | 50-90 | rpm |