LNP THERMOCOMP DF0029ER 含有10%玻璃纤维的聚碳酸酯树脂

¥98.00 ≥25千克起批

参数

否是否进口
中国厂家(产地)
DF0029ER牌号

发货地广东东莞不限

东莞市聚浩塑化有限公司 2年: 进入店铺在线咨询

LNP THERMOCOMP DF0029P 10%玻璃纤维的聚碳酸酯树脂 ¥98.00

LNP THERMOCOMP DF002ER 含有10%玻璃纤维的聚碳酸酯 ¥98.00

LNP THERMOCOMP DF002ERH 含有10%玻璃纤维的聚碳酸酯树脂 ¥98.00

LNP Thermocomp DF002FV 10%玻璃纤维增强、冲击改性的PC树脂基LDS材料 ¥98.00

LNP THERMOCOMP DF002H 含有10%玻璃纤维的聚碳酸酯树脂 ¥98.00

LNP THERMOCOMP DF003E 含有15%玻璃纤维的聚碳酸酯树脂 ¥78.00

产品详情

PROPERTIES		TYPICAL VALUES	UNITS	TEST METHODS
FLAME CHARACTERISTICS	¹⁾
UL Yellow Card Link		E121562-101344533	-	-
UL Recognized, 94V-1 Flame Class Rating		≥3	mm	UL 94
UL Recognized, 94V-2 Flame Class Rating		≥1.5	mm	UL 94
ELECTRICAL	¹⁾
High Voltage Arc Track Rate {PLC}		4	PLC Code	UL 746A
Hot-Wire Ignition (HWI), PLC 0		≥1.5	mm	UL 746A
High Amp Arc Ignition (HAI), PLC 2		≥3	mm	UL 746A
High Amp Arc Ignition (HAI), PLC 4		≥1.5	mm	UL 746A
MECHANICAL	²⁾
Tensile Stress, yld, Type I, 5 mm/min		81	MPa	ASTM D638
Tensile Stress, brk, Type I, 5 mm/min		75	MPa	ASTM D638
Tensile Strain, yld, Type I, 5 mm/min		3.9	%	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min		5.6	%	ASTM D638
Tensile Modulus, 50 mm/min		4250	MPa	ASTM D638
Flexural Stress, yld, 1.3 mm/min, 50 mm span		138	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span		4110	MPa	ASTM D790
Tensile Stress, yield, 5 mm/min		80	MPa	*** 527
Tensile Stress, break, 5 mm/min		74	MPa	*** 527
Tensile Strain, yield, 5 mm/min		3.8	%	*** 527
Tensile Strain, break, 5 mm/min		5.7	%	*** 527
Tensile Modulus, 1 mm/min		4170	MPa	*** 527
Flexural Modulus, 2 mm/min		3950	MPa	*** 178
IMPACT	²⁾
Izod Impact, unnotched, 23°C		883	J/m	ASTM D4812
Izod Impact, notched, 23°C		81	J/m	ASTM D256
Multiaxial Impact		10	J	*** 6603
Instrumented Dart Impact Total Energy, 23°C		18	J	ASTM D3763
Izod Impact, unnotched 80104 +23°C		54	kJ/m²	*** 180/1U
Izod Impact, notched 80104 +23°C		8	kJ/m²	*** 180/1A
THERMAL	²⁾
HDT, 0.45 MPa, 3.2 mm, unannealed		146	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed		141	°C	ASTM D648
CTE, -30°C to 30°C, flow		4.5E-05	1/°C	ASTM D696
CTE, -30°C to 30°C, xflow		5.3E-05	1/°C	ASTM D696
HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm		146	°C	*** 75/Bf
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm		141	°C	*** 75/Af
Relative Temp Index, Elec	¹⁾	125	°C	UL 746B
Relative Temp Index, Mech w/impact	¹⁾	115	°C	UL 746B
Relative Temp Index, Mech w/o impact	¹⁾	125	°C	UL 746B
PHYSICAL	²⁾
Density		1.29	g/cm³	ASTM D792
Moisture Absorption, (23°C/50% RH/24 hrs)		0.14	%	ASTM D570
Mold Shrinkage, flow, 24 hrs	⁴⁾	0.4-0.6	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	⁴⁾	0.6-0.8	%	ASTM D955
Density		1.29	g/cm³	*** 1183
Moisture Absorption (23°C / 50% RH)		0.2	%	*** 62
INJECTION MOLDING	³⁾
Drying Temperature		120	°C
Drying Time		4	Hrs
Maximum Moisture Content		0.02	%
Melt Temperature		305-325	°C
Front - Zone 3 Temperature		320-330	°C
Middle - Zone 2 Temperature		310-320	°C
Rear - Zone 1 Temperature		295-305	°C
Mold Temperature		80-110	°C
Back Pressure		0.2-0.3	MPa
Screw Speed		30-60	rpm

为您推荐

LNP THERMOCOMP DF004 含有20%玻璃纤维的聚碳酸酯 ¥78.00
LNP THERMOCOMP DF0046P 含有20%玻璃纤维的聚碳酸酯树脂 ¥78.00
LNP THERMOCOMP DF0049 含有20%玻璃纤维的聚碳酸酯树脂 ¥87.00
LNP THERMOCOMP DF0049P 含有20%玻璃纤维的聚碳酸酯 ¥87.00
LNP THERMOCOMP DF004ER 20%玻璃纤维的聚碳酸酯树脂 ¥78.00
LNP THERMOCOMP DF004P 含有20%玻璃纤维的聚碳酸酯树脂 ¥87.00

LNP Thermocomp DF004RXP 含有20%玻璃纤维的聚碳酸酯树脂 ¥98.00
LNP THERMOCOMP DF004XXC 含玻璃纤维的聚碳酸酯化合物 ¥129.00
LNP THERMOCOMP DF005 25%的玻璃纤维PC ¥98.00
LNP THERMOCOMP DF006 含有30%玻璃纤维的聚碳酸酯 ¥98.00
LNP THERMOCOMP DF0069P 含有30%玻璃纤维的聚碳酸酯树脂 ¥158.00
LNP THERMOCOMP DF006ER 含有30%玻璃纤维的聚碳酸酯树脂 ¥78.00

LNP THERMOCOMP DF006HL 含有30%玻璃纤维的聚碳酸酯树脂 ¥98.00
LNP THERMOCOMP DF006LXN 基于含有30%玻璃纤维的聚碳酸酯树脂 ¥118.00
LNP THERMOCOMP DF008 含有40%的玻璃纤维 ¥78.00
LNP THERMOCOMP DF0081PI 含有玻璃纤维，阻燃剂 ¥78.00
LNP THERMOCOMP DF0084 含有玻璃纤维，阻燃剂 ¥78.00
LNP THERMOCOMP DF008ER 基于聚碳酸酯树脂的化合物，含有40%的玻璃纤维 ¥78.00

供应商网> 特种塑料> LNP THERMOCOMP DF0029ER 含有10%玻璃纤维的聚碳酸酯树脂

在线问

产品参数

是否进口否
厂家(产地)中国
牌号DF0029ER
用途级别注塑

1/2

¥98.00 在线咨询

进店客服获取最低报价拨打电话

LNP THERMOCOMP DF0029ER 含有10%玻璃纤维的聚碳酸酯树脂: ¥98.00