LNP THERMOCOMP DF006ER 含有30%玻璃纤维的聚碳酸酯树脂

¥78.00 ≥25千克起批

参数

否是否进口
中国厂家(产地)
DF006ER牌号

发货地广东东莞不限

东莞市聚浩塑化有限公司 2年: 进入店铺在线咨询

LNP THERMOCOMP DF006HL 含有30%玻璃纤维的聚碳酸酯树脂 ¥98.00

LNP THERMOCOMP DF006LXN 基于含有30%玻璃纤维的聚碳酸酯树脂 ¥118.00

LNP THERMOCOMP DF008 含有40%的玻璃纤维 ¥78.00

LNP THERMOCOMP DF0081PI 含有玻璃纤维，阻燃剂 ¥78.00

LNP THERMOCOMP DF0084 含有玻璃纤维，阻燃剂 ¥78.00

LNP THERMOCOMP DF008ER 基于聚碳酸酯树脂的化合物，含有40%的玻璃纤维 ¥78.00

产品详情

PROPERTIES		TYPICAL VALUES	UNITS	TEST METHODS
FLAME CHARACTERISTICS	¹⁾
UL Yellow Card Link		E121562-101284106	-	-
UL Recognized, 94V-0 Flame Class Rating		≥3	mm	UL 94
UL Recognized, 94V-2 Flame Class Rating		≥1.5	mm	UL 94
MECHANICAL	²⁾
Tensile Stress, brk, Type I, 5 mm/min		132	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min		2.7	%	ASTM D638
Tensile Modulus, 5 mm/min		9500	MPa	ASTM D638
Flexural Strength, 1.3 mm/min, 50 mm span		190	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span		8400	MPa	ASTM D790
Tensile Stress, break, 5 mm/min		125	MPa	ISO 527
Tensile Strain, break, 5 mm/min		2.2	%	ISO 527
Tensile Modulus, 1 mm/min		9000	MPa	ISO 527
Flexural Strength, 2 mm/min		185	MPa	ISO 178
Flexural Modulus, 2 mm/min		7800	MPa	ISO 178
IMPACT	²⁾
Izod Impact, unnotched, 23°C		865	J/m	ASTM D4812
Izod Impact, notched, 23°C		133	J/m	ASTM D256
Instrumented Dart Impact Energy @ peak, 23°C		8	J	ASTM D3763
Multiaxial Impact		4	J	ISO 6603
Izod Impact, unnotched 80104 +23°C		60	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C		13	kJ/m²	ISO 180/1A
THERMAL	²⁾
HDT, 1.82 MPa, 3.2mm, unannealed		136	°C	ASTM D648
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm		140	°C	ISO 75/Af
Relative Temp Index, Elec	¹⁾	80	°C	UL 746B
Relative Temp Index, Mech w/impact	¹⁾	80	°C	UL 746B
Relative Temp Index, Mech w/o impact	¹⁾	80	°C	UL 746B
PHYSICAL	²⁾
Density		1.42	g/cm³	ASTM D792
Moisture Absorption, (23°C/50% RH/24 hrs)		0.1	%	ASTM D570
Mold Shrinkage, flow, 24 hrs	⁴⁾	0.1	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	⁴⁾	0.5	%	ASTM D955
Mold Shrinkage, flow, 24 hrs	⁴⁾	0.11	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	⁴⁾	0.48	%	ISO 294
Density		1.42	g/cm³	ISO 1183
INJECTION MOLDING	³⁾
Drying Temperature		120	°C
Drying Time		4	Hrs
Maximum Moisture Content		0.02	%
Melt Temperature		305-325	°C
Front - Zone 3 Temperature		320-330	°C
Middle - Zone 2 Temperature		310-320	°C
Rear - Zone 1 Temperature		295-305	°C
Mold Temperature		80-110	°C
Back Pressure		0.2-0.3	MPa
Screw Speed		30-60	rpm

为您推荐

LNP THERMOCOMP DF008ERH 含有40%玻璃纤维的聚碳酸酯 ¥78.00
LNP Thermocomp DF00AIP 含有玻璃纤维，阻燃剂 ¥98.00
LNP THERMOCOMP DF00A8P 高模量、良好的平整度、良好的冲击性能 ¥78.00
LNP THERMOCOMP DFZ22P 含有10%玻璃纤维和10%研磨玻璃 ¥78.00
LNP THERMOCOMP DX05474 阻燃 ¥87.00
LNP THERMOCOMP DX05477 易于成型、脱模、阻燃 ¥78.00

LNP THERMOCOMP DX06094 高冲击，非溴化和非氯化阻燃剂和脱模剂 ¥78.00
LNP THERMOCOMP DX06313 30%玻璃纤维增强，抗冲改性材料 ¥78.00
LNP THERMOCOMP DX06313I 高流动性和良好的延展性 ¥87.00
LNP THERMOCOMP DX06408 含有20%玻璃纤维的聚碳酸酯树脂 ¥87.00
LNP THERMOCOMP DX06409 含有10%玻璃纤维的聚碳酸酯树脂 ¥87.00
LNP THERMOCOMP DX06410 含有20%玻璃纤维的聚碳酸酯树脂 ¥78.00

供应商网> 特种塑料> LNP THERMOCOMP DF006ER 含有30%玻璃纤维的聚碳酸酯树脂

在线问

产品参数

是否进口否
厂家(产地)中国
牌号 DF006ER
用途级别注塑

1/2

¥78.00 在线咨询

进店客服获取最低报价拨打电话

LNP THERMOCOMP DF006ER 含有30%玻璃纤维的聚碳酸酯树脂: ¥78.00