PROPERTIES |
| TYPICAL VALUES | UNITS | TEST METHODS |
---|
MECHANICAL | 1) |
|
|
|
---|
Tensile Stress, break, 5 mm/min |
| 181 | MPa | ISO 527 |
---|
Tensile Strain, break, 5 mm/min |
| 3.7 | % | ISO 527 |
---|
Tensile Modulus, 1 mm/min |
| 10900 | MPa | ISO 527 |
---|
Flexural Stress, yield, 2 mm/min |
| 265 | MPa | ISO 178 |
---|
Flexural Modulus, 2 mm/min |
| 10600 | MPa | ISO 178 |
---|
IMPACT | 1) |
|
|
|
---|
Izod Impact, unnotched 80*10*4 +23°C |
| 95 | kJ/m² | ISO 180/1U |
---|
Izod Impact, notched 80*10*4 +23°C |
| 19 | kJ/m² | ISO 180/1A |
---|
THERMAL | 1) |
|
|
|
---|
CTE, 23°C to 60°C, flow |
| 1.7E-05 | 1/°C | ISO 11359-2 |
---|
CTE, 23°C to 60°C, xflow |
| 9.3E-05 | 1/°C | ISO 11359-2 |
---|
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm |
| 203 | °C | ISO 75/Af |
---|
PHYSICAL | 1) |
|
|
|
---|
Mold Shrinkage on Tensile Bar, flow | 3) | 0.2-0.4 | % | SABIC method |
---|
Density |
| 1.51 | g/cm³ | ISO 1183 |
---|
产品参数
- 否
- 中国
- QF00A
- 注塑
- LNP THERMOCOMP QF00A 含有50%玻璃纤维的尼龙6/10