产品详情
PROPERTIES |
| TYPICAL VALUES | UNITS | TEST METHODS |
---|
FLAME CHARACTERISTICS | 1) |
|
|
|
---|
UL Yellow Card Link |
| E121562-221093 | - | - |
---|
UL Recognized, 94-5VA Flame Class Rating |
| ≥1.9 | mm | UL 94 |
---|
UL Recognized, 94V-0 Flame Class Rating |
| ≥0.41 | mm | UL 94 |
---|
MECHANICAL |
|
|
|
|
---|
Tensile Stress, yld, Type I, 5 mm/min |
| 131 | MPa | ASTM D638 |
---|
Tensile Stress, brk, Type I, 5 mm/min |
| 131 | MPa | ASTM D638 |
---|
Tensile Strain, yld, Type I, 5 mm/min |
| 4 | % | ASTM D638 |
---|
Tensile Strain, brk, Type I, 5 mm/min |
| 4 | % | ASTM D638 |
---|
Tensile Modulus, 5 mm/min |
| 6890 | MPa | ASTM D638 |
---|
Flexural Stress, yld, 1.3 mm/min, 50 mm span |
| 225 | MPa | ASTM D790 |
---|
Flexural Modulus, 1.3 mm/min, 50 mm span |
| 6850 | MPa | ASTM D790 |
---|
Tensile Stress, yield, 5 mm/min |
| 131 | MPa | ISO 527 |
---|
Tensile Stress, break, 5 mm/min |
| 131 | MPa | ISO 527 |
---|
Tensile Strain, yield, 5 mm/min |
| 4 | % | ISO 527 |
---|
Tensile Strain, break, 5 mm/min |
| 4 | % | ISO 527 |
---|
Tensile Modulus, 1 mm/min |
| 6890 | MPa | ISO 527 |
---|
Flexural Stress, yield, 2 mm/min |
| 228 | MPa | ISO 178 |
---|
Flexural Modulus, 2 mm/min |
| 6890 | MPa | ISO 178 |
---|
IMPACT |
|
|
|
|
---|
Izod Impact, unnotched, 23°C |
| 480 | J/m | ASTM D4812 |
---|
Izod Impact, notched, 23°C |
| 64 | J/m | ASTM D256 |
---|
Izod Impact, notched, -30°C |
| 70 | J/m | ASTM D256 |
---|
Instrumented Dart Impact Total Energy, 23°C |
| 8 | J | ASTM D3763 |
---|
Izod Impact, notched 80*10*4 +23°C |
| 64 | kJ/m² | ISO 180/1A |
---|
Izod Impact, notched 80*10*4 -30°C |
| 70 | kJ/m² | ISO 180/1A |
---|
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm |
| 65 | kJ/m² | ISO 179/1eA |
---|
THERMAL |
|
|
|
|
---|
Vicat Softening Temp, Rate B/50 |
| 220 | °C | ASTM D1525 |
---|
HDT, 1.82 MPa, 3.2mm, unannealed |
| 208 | °C | ASTM D648 |
---|
CTE, -40°C to 150°C, xflow |
| 4.9E-05 | 1/°C | ASTM E831 |
---|
CTE, -20°C to 150°C, flow |
| 2.1E-05 | 1/°C | ASTM E831 |
---|
CTE, 23°C to 150°C, flow |
| 2.1E-05 | 1/°C | ISO 11359-2 |
---|
CTE, 23°C to 150°C, xflow |
| 4.9E-05 | 1/°C | ISO 11359-2 |
---|
Vicat Softening Temp, Rate B/50 |
| 212 | °C | ISO 306 |
---|
Vicat Softening Temp, Rate B/120 |
| 218 | °C | ISO 306 |
---|
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm |
| 205 | °C | ISO 75/Ae |
---|
Relative Temp Index, Elec | 1) | 170 | °C | UL 746B |
---|
Relative Temp Index, Mech w/impact | 1) | 170 | °C | UL 746B |
---|
Relative Temp Index, Mech w/o impact | 1) | 170 | °C | UL 746B |
---|
PHYSICAL |
|
|
|
|
---|
Specific Gravity |
| 1.42 | - | ASTM D792 |
---|
Mold Shrinkage, flow, 3.2 mm |
| 0.3-0.5 | % | SABIC method |
---|
Melt Flow Rate, 337°C/6.6 kgf |
| 6 | g/10 min | ASTM D1238 |
---|
Density |
| 1.42 | g/cm³ | ISO 1183 |
---|
Water Absorption, (23°C/saturated) |
| 1 | % | ISO 62-1 |
---|
Moisture Absorption (23°C / 50% RH) |
| 0.55 | % | ISO 62 |
---|
Melt Volume Rate, MVR at 360°C/5.0 kg |
| 7 | cm³/10 min | ISO 1133 |
---|
ELECTRICAL |
|
|
|
|
---|
Comparative Tracking Index (UL) {PLC} |
| 4 | PLC Code | UL 746A |
---|
Hot-Wire Ignition (HWI), PLC 1 |
| ≥3 | mm | UL 746A |
---|
Hot-Wire Ignition (HWI), PLC 2 |
| ≥1.5 | mm | UL 746A |
---|
High Amp Arc Ignition (HAI), PLC 3 |
| ≥1.5 | mm | UL 746A |
---|
High Amp Arc Ignition (HAI), PLC 4 |
| ≥3 | mm | UL 746A |
---|
High Voltage Arc Track Rate {PLC} |
| 2 | PLC Code | UL 746A |
---|
Arc Resistance, Tungsten {PLC} |
| 6 | PLC Code | ASTM D495 |
---|
INJECTION MOLDING |
|
|
|
|
---|
Drying Temperature |
| 150 | °C |
|
---|
Drying Time |
| 4-6 | Hrs |
|
---|
Drying Time (Cumulative) |
| 24 | Hrs |
|
---|
Maximum Moisture Content |
| 0.02 | % |
|
---|
Melt Temperature |
| 350-400 | °C |
|
---|
Nozzle Temperature |
| 345-400 | °C |
|
---|
Front - Zone 3 Temperature |
| 345-400 | °C |
|
---|
Middle - Zone 2 Temperature |
| 340-400 | °C |
|
---|
Rear - Zone 1 Temperature |
| 330-400 | °C |
|
---|
Mold Temperature |
| 135-165 | °C |
|
---|
Back Pressure |
| 0.3-0.7 | MPa |
|
---|
Screw Speed |
| 40-70 | rpm |
|
---|
Shot to Cylinder Size |
| 40-60 | % |
|
---|
Vent Depth |
| 0.025-0.076 | mm |
|
---|
产品参数
- 否
- 中国
- HU2200
- 注塑
- ULTEM HU2200 20%玻璃纤维填充,增强流动性聚醚酰亚胺