Density(23°C) | 1.35 | g/cm | ISO 1183 |
Molding Shrinkage | ISO 294-4 | ||
Across Flow : 23°C | 0.80 | % | |
Flow : 23°C | 0.30 | % | |
Water Absorption | ISO 62 | ||
24 hr, 23°C | 1.9 | % | |
Saturation, 23°C | 5.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus(23°C) | 8000 | MPa | ISO 527-2 |
Tensile Stress(Yield, 23°C) | 170 | MPa | ISO 527-2 |
Tensile Strain(Break, 23°C) | 4.5 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength | ISO 179/1eA | ||
-30°C | 6.0 | kJ/m | |
23°C | 12 | kJ/m | |
Charpy Unnotched Impact Strength | ISO 179/1eU | ||
-30°C | No Break | ||
23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
Heat Deflection Temperature | |||
0.45 MPa, Unannealed | 220 | °C | ISO 75-2/B |
1.8 MPa, Unannealed | 210 | °C | ISO 75-2/A |
Continuous Use Temperature3 | 110 | °C | IEC 60216 |
Ball Pressure Test | IEC 60695-10-2 | ||
125°C | Pass | ||
165°C | Pass |
| Electrical | Nominal Value | Unit | Test Method |
Surface Resistivity4 | 1.0E+13 | ohms | IEC 60093 |
Volume Resistivity(23°C) | 1.0E+15 | ohms·cm | IEC 60093 |
Electric Strength(2.00 mm) | 18 | kV/mm | IEC 60243-1 |
Comparative Tracking Index(3.20 mm, Solution A) | 600 | V | IEC 60112 |
Needle Flame Test | IEC 60695-11-5 | ||
1.00 mm | Pass | ||
2.00 mm | Pass | ||
| Flammability | Nominal Value | Unit | Test Method |
Flame Rating | UL 94 | ||
0.40 mm, BK | V-0 | ||
0.8 mm | V-0 | ||
1.6 mm | V-0 | ||
3.2 mm | V-0 |
PA6汽车领域中的应用
内外饰部件
汽车用***增强PA6复合材料具有***的耐气候性、良好的油漆性能和杰出的表现效果，为了满足在内外饰方面的使用要求，增强PA6材料应具备以下要求：
1). 高耐热，长期使用；
2）***的刚性和韧性的结合；
3). 能够满足强烈的温度和湿度的不断变化而承受巨大的应变；
4). ***尺寸稳定性，具有防翘曲的效果；
5). 具有高表面质量，表面光洁。
在线问