热稳定PA6 OMNILON PA6 GR25 HSX塞拉尼斯
ISO | Value | Unit | Test Standard |
Density | 1300 | kg/m | ISO 1183 |
Tensile modulus | 9000 | MPa | ISO 527-2/1A |
Tensile stress at break, 5mm/min | 170 | MPa | ISO 527-2/1A |
Tensile strain at break, 5mm/min | 3.8 | % | ISO 527-2/1A |
Flexural modulus, 23°C | 8750 | MPa | ISO 178 |
Flexural strength, 23°C | 280 | MPa | ISO 178 |
Charpy notched impact strength, 23°C | 12 | kJ/m | ISO 179/1eA |
DTUL at 1.8 MPa | 204 | °C | ISO 75-1, -2 |
DTUL at 0.45 MPa | 218 | °C | ISO 75-1, -2 |
Temperature | Value | Unit | Test Standard |
Zone1 temperature | 220 - 230 | °C | - |
Zone2 temperature | 225 - 235 | °C | - |
Zone3 temperature | 235 - 245 | °C | - |
Zone4 temperature | 245 - 255 | °C | - |
Nozzle temperature | 255 - 270 | °C | - |
Melt temperature | 250 - 270 | °C | - |
Mold temperature | 60 - 80 | °C | - |
Hot runner temperature | 255 - 270 | °C | - |
PA6汽车领域中的应用
内外饰部件
汽车用***增强PA6复合材料具有***的耐气候性、良好的油漆性能和杰出的表现效果,为了满足在内外饰方面的使用要求,增强PA6材料应具备以下要求:
1). 高耐热,长期使用;
2)***的刚性和韧性的结合;
3). 能够满足强烈的温度和湿度的不断变化而承受巨大的应变;
4). ***尺寸稳定性,具有防翘曲的效果;
5). 具有高表面质量,表面光洁。