| Density | 1.35g/cc | 0.0488lb/in | *** 1183 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 145MPa | 21000psi | *** 527 |
| Elongation at Break | 2.40 % | 2.40 % | *** 527 |
| Tensile Modulus | 8.50GPa | 1230ksi | *** 527 |
| Flexural Modulus | 7.90GPa | 1150ksi | *** 178 |
| Izod Impact, Notched (***) | 7.70kJ/m | 3.66ft-lb/in | *** 180 |
| Charpy Impact, Notched | 0.850J/cm | 4.04ft-lb/in | *** 179 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 260°C | 500°F | *** 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 245°C | 473°F | *** 75 |
| UL RTI, Electrical | 130°C @Thickness 0.750 mm | 266°F @Thickness 0.0295 in | UL746B |
| 130°C @Thickness 1.50 mm | 266°F @Thickness 0.0591 in | UL746B | |
| 130°C @Thickness 3.00 mm | 266°F @Thickness 0.118 in | UL746B | |
| UL RTI, Mechanical with Impact | 115°C @Thickness 0.750 mm | 239°F @Thickness 0.0295 in | UL746B |
| 115°C @Thickness 1.50 mm | 239°F @Thickness 0.0591 in | UL746B | |
| 115°C @Thickness 3.00 mm | 239°F @Thickness 0.118 in | UL746B | |
| UL RTI, Mechanical without Impact | 140°C @Thickness 0.750 mm | 284°F @Thickness 0.0295 in | UL746B |
| 140°C @Thickness 1.50 mm | 284°F @Thickness 0.0591 in | UL746B | |
| 140°C @Thickness 3.00 mm | 284°F @Thickness 0.118 in | UL746B | |
| Flammability, UL94 | HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | |
| V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | ||
| V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | ||