Density | 1.10 | -- | g/cm | *** 1183/A |
Water Absorption(24 hr, 23°C) | 1.1 | -- | % | *** 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
Tensile Modulus(23°C) | 2550 | 1400 | MPa | *** 527-2/1A |
Tensile Stress | *** 527-2/1A | |||
Yield, 23°C | 70.0 | 40.0 | MPa | |
Break, 23°C | 50.0 | 40.0 | MPa | |
Tensile Strain | *** 527-2 | |||
Yield, 23°C | 5.0 | 15 | % | |
Break, 23°C | 30 | -- | % | |
Flexural Modulus(23°C) | 2250 | 1200 | MPa | *** 178 |
Flexural Stress(23°C) | 95.0 | 47.0 | MPa | *** 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
Charpy Notched Impact Strength(23°C) | 10 | 20 | kJ/m | *** 179/1eA |
Charpy Unnotched Impact Strength(23°C) | No Break | -- | *** 179/1eU | |
Notched Izod Impact Strength(23°C) | 8.0 | 16 | kJ/m | *** 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
Heat Deflection Temperature(1.8 MPa, Unannealed) | 70.0 | -- | °C | *** 75-2/Af |
Melting Temperature | 263 | -- | °C | *** 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
Surface Resistivity | 1.0E+15 | 1.0E+15 | ohms | IEC 60093 |
Volume Resistivity | 1.0E+15 | 1.0E+15 | ohms·cm | IEC 60093 |
Electric Strength | IEC 60243-1 | |||
23°C, 0.800 mm | 35 | -- | kV/mm | |
23°C, 2.00 mm | 22 | -- | kV/mm | |
Relative Permittivity(23°C, 2.00 mm, 1 MHz) | 3.50 | -- | IEC 60250 | |
Dissipation Factor(1 MHz) | 0.033 | -- | IEC 60250 | |
Comparative Tracking Index | IEC 60112 | |||
Solution A | 500 | -- | V | |
Solution B | 475 | -- | V |
***PA，导电PA，加纤防火PA，防火PA，抗紫外线耐候PA，高温挤出级PA。
导电尼龙66：具有良好的***性、耐热性、耐油性及耐化学药品性，还大大降低了原材料的吸水率和收缩率,具有优良的尺寸稳定性及***的机械强度。能满足静电消散和静电放电(ESD)防护的要求。这些特殊改性材料经特殊配制，适用于从100到1012欧姆/平方(ohms/sq)的表面电阻范围，可用于注塑及挤出等成型。有很多超越金属和涂装的优点:零件重量较轻，较易处理，运输***较低。它们的装配简便，制造***较低，并且较不会受到撞凹，割损和刮伤。为了标识或美观目的，一些材料可被预先染色，避免费时且昂贵的两次着色加工。