增韧高刚PA66 Bergamid A65 G25 SO普立万
Density | 1.31 | g/cm³ | ISO 1183 |
Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus | 8200 | MPa | ISO 527-1/1 |
Tensile Stress | 160 | MPa | ISO 527-2/5 |
Tensile Strain (Break) | 3.0 | % | ISO 527-2/5 |
Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength (23°C) | 7.0 | kJ/m² | ISO 179 |
Charpy Unnotched Impact Strength (23°C) | 60 | kJ/m² | ISO 179 |
Thermal | Nominal Value | Unit | |
Melting Temperature | 260 to 265 | °C |
Injection | Nominal Value | Unit | |
Drying Temperature | 80 to 90 | °C | |
Drying Time | 2.0 to 4.0 | hr | |
Rear Temperature | 275 to 285 | °C | |
Middle Temperature | 280 to 290 | °C | |
Front Temperature | 285 to 295 | °C | |
Nozzle Temperature | 295 to 300 | °C | |
Mold Temperature | 80 | °C |