原包科思创抗紫外线PC APEC 1697耐温157度
Density(23°C) | 1.18 | g/cm | ISO 1183 |
Melt Mass-Flow Rate (MFR)(330°C/2.16 kg) | 46 | g/10 min | ISO 1133 |
Melt Volume-Flow Rate (MVR)(330°C/2.16 kg) | 45 | cm/10min | ISO 1133 |
Tensile Modulus(23°C) | 2400 | MPa | ISO 527-2/1 |
Tensile Stress(Yield, 23°C) | 68.0 | MPa | ISO 527-2/50 |
Tensile Strain(Yield, 23°C) | 6.2 | % | ISO 527-2/50 |
Nominal Tensile Strain at Break(23°C) | > 50 | % | ISO 527-2/50 |
Heat Deflection Temperature | |||
0.45 MPa, Unannealed | 149 | °C | ISO 75-2/B |
1.8 MPa, Unannealed | 137 | °C | ISO 75-2/A |
Vicat Softening Temperature | 157 | °C | ISO 306/B120 |
Flame Rating | UL 94 | ||
1.5 mm | HB | ||
3.0 mm | HB |
Optical | Nominal Value | Unit | Test Method |
Refractive Index2 | 1.578 | ISO 489 | |
Light Transmittance(1000 m) | 89.0 | % | ISO 13468-2 |