40%玻纤高刚防火EMERGE PC 8704盛禧奥
Density / Specific Gravity | 1.50 | g/cm³ | ASTM D792 |
Molding Shrinkage | ASTM D955 | ||
Flow | 0.20 to 0.40 | % | |
Across Flow | 0.20 to 0.40 | % |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus 3 | 6500 | MPa | ASTM D638 |
Tensile Strength 4 (Break) | 137 | MPa | ASTM D638 |
Tensile Elongation 4 (Break) | 1.7 | % | ASTM D638 |
Flexural Modulus 5 | 11700 | MPa | ASTM D790 |
Flexural Strength 5 | 206 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
Notched Izod Impact (23°C) | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load | ASTM D648 | ||
0.45 MPa, Unannealed | 135 | °C | |
0.45 MPa, Annealed | 140 | °C | |
1.8 MPa, Unannealed | 133 | °C | |
1.8 MPa, Annealed | 136 | °C | |
Vicat Softening Temperature | |||
-- | 141 | °C | ASTM D1525 6 |
-- | 152 | °C | ASTM D1525 7 |
| Flammability | Nominal Value | Test Method | |
Flame Rating 8 | UL 94 | ||
1.5 mm | V-1 | ||
2.0 mm | V-0 |