Density / Specific Gravity | 1.14 | g/cm³ | ASTM D792, *** 1183 |
Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 22 | g/10 min | ASTM D1238 |
Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 18 | cm³/10min | *** 1133 |
Molding Shrinkage | Internal Method | ||
Across Flow : 3.20 mm | 0.50 to 0.70 | % | |
Flow : 3.20 mm | 0.50 to 0.70 | % | |
Water Absorption | *** 62 | ||
Saturation, 23°C | 0.40 | % | |
Equilibrium, 23°C, 50% RH | 0.15 | % |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus | |||
-- 1 | 2300 | MPa | ASTM D638 |
-- | 2200 | MPa | *** 527-2/1 |
Tensile Strength | |||
Yield 2 | 55.0 | MPa | ASTM D638 |
Yield | 54.0 | MPa | *** 527-2/50 |
Break 2 | 52.0 | MPa | ASTM D638 |
Break | 51.0 | MPa | *** 527-2/50 |
Charpy Notched Impact Strength | |||
-30°C 6 | 45 | kJ/m² | *** 179/1eA |
23°C 6 | 60 | kJ/m² | *** 179/1eA |
23°C 7 | 70 | kJ/m² | *** 179/1eA |
Heat Deflection Temperature | |||
0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span 8 | 126 | °C | *** 75-2/Bf |
1.8 MPa, Unannealed, 3.20 mm | 107 | °C | ASTM D648 |
1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 8 | 105 | °C | *** 75-2/Af |