40%玻纤PPO NORYL PPX640F
¥45.80
高抗冲击PPE/PS NORYL PPX7115F
¥45.80
阻燃耐水解PPE/PS NORYL NH4050
¥44.50
导电耐热PPE/PA NORYL GTXNX0031
¥47.80
50%玻纤增强PPE/PS NORYL CN5260
¥28.50
40GF增强PPE/PS NORYL CN5258
¥45.80
沙伯基础30GF增强PPE/PP NORYL PPX630F
| 备注说明 | 填料：玻璃纤维增强材料, 30% 填料按重量。 | ||
| 物理性能 | 比重 | ASTMD792 | 1.19 | g/cm | |
| 熔流率（熔体流动速率）(260°C/5.0kg) | ASTMD1238 | 2.6 | g/10min | ||
| 收缩率-流动(3.20mm) | InternalMethod | 0.20to0.23 | % | ||
| MoldingShrinkage-AcrossFlow(3.20mm) | InternalMethod | 0.25to0.76 | % | ||
| 机械性能 | 抗张强度2(屈服) | ASTMD638 | 79.3 | MPa | |
| 抗张强度2(断裂) | ASTMD638 | 79.3 | MPa | ||
| 伸长率2(断裂) | ASTMD638 | 7.7 | % | ||
| 弯曲模量4(50.0mm跨距) | ASTMD790 | 5560 | MPa | ||
| FlexuralStrength3(Break,50.0mmSpan) | ASTMD790 | 130 | MPa | ||
| 冲击性能 | 悬壁梁缺口冲击强度 | -30°C | ASTMD256 | 100 | J/m |
| 23°C | ASTMD256 | 170 | J/m | ||
| 悬壁梁缺口冲击强度(23°C) | ASTMD4812 | 830 | J/m | ||
| 装有测量仪表的落镖冲击 | -30°C,TotalEnergy | ASTMD3763 | 20.4 | J | |
| 23°C,TotalEnergy | ASTMD3763 | 19.1 | J | ||
| 热性能 | 载荷下热变形温度(0.45MPa,未退火,3.20mm) | ASTMD648 | 155 | °C | |
| 载荷下热变形温度(1.8MPa,未退火,3.20mm) | ASTMD648 | 134 | °C | ||
| 维卡软化温度 | ASTMD15254 | 162 | °C | ||
| 线形热膨胀系数-流动(-40到40°C) | ASTME831 | 1.4E-5 | cm/cm/°C | ||
| 线形热膨胀系数-横向(-40到40°C) | ASTME831 | 7.7E-5 | cm/cm/°C | ||
| 可燃性 | UL阻燃等级(1.5mm) | UL94 | HB |
PPO可以与ABS,HDPE,PPS,PA,HIPS、玻璃纤维等进行共混改性处理。PPO塑胶原料特性A、PPO塑胶原料***、透明、相对密度小，具有优良的机械强度、耐应力松弛、耐蠕变性、耐热性、耐水性、耐水蒸汽性、尺寸稳定性。B、在很宽温度、频变范围内电性能好，不水解、成型收缩率小，难燃有自熄性，耐无机酸、碱、耐芳香烃、卤代烃、油类等性能差，易溶胀或应力开裂。C、它具有刚性大、耐热性高、难燃、强度较高电性能优良等优点。D、PPO还具有***、***、耐污染等优点。E、PPO塑胶原料的介电常数和介电损耗在工程塑料中是***小的品种之一，几乎不受温度、湿度的影响，可用于低、中、高频电场领域。F、PPO的负荷变形温度可达190℃以上，脆化温度为-170℃。 G、主要缺点是熔融流动性差，加工成型困难。