沙伯基础高抗冲击PPE/PS NORYL PPX7115F
| 规格级别 | 抗撞击性，高,耐热性，高 注射成型 |
| 物理性能 | 比重 | ASTMD792 | 0.988 | g/cm | |
| 熔流率（熔体流动速率）(260°C/5.0kg) | ASTMD1238 | 14 | g/10min | ||
| 溶化体积流率（MVR）(260°C/5.0kg) | ***1133 | 12.0 | cm/10min | ||
| 收缩率-流动(3.20mm) | InternalMethod | 0.60to0.70 | % | ||
| MoldingShrinkage-AcrossFlow(3.20mm) | InternalMethod | 0.60to0.80 | % | ||
| 机械性能 | 拉伸模量2 | ASTMD638 | 1240 | MPa | |
| 拉伸模量 | ***527-2/1 | 1380 | MPa | ||
| 抗张强度3(屈服) | ASTMD638 | 35.9 | MPa | ||
| 拉伸应力(屈服) | ***527-2/50 | 35.0 | MPa | ||
| 抗张强度3(断裂) | ASTMD638 | 34.5 | MPa | ||
| 伸长率3(屈服) | ASTMD638 | 8.0 | % | ||
| 伸长率4(断裂) | ASTMD638 | 130 | % | ||
| 拉伸应变(断裂) | ***527-2/50 | 75 | % | ||
| 弯曲模量4(50.0mm跨距) | ASTMD790 | 1380 | MPa | ||
| 弯曲强度4(屈服,50.0mm跨距) | ASTMD790 | 51.7 | MPa | ||
| 冲击性能 | 悬壁梁缺口冲击强度(23°C) | ASTMD256 | 530 | J/m | |
| 装有测量仪表的落镖冲击 | -30°C,TotalEnergy | ASTMD3763 | 30.0 | J | |
| 23°C,TotalEnergy | ASTMD3763 | 37.0 | J | ||
| 热性能 | 载荷下热变形温度(0.45MPa,未退火,3.20mm) | ASTMD648 | 113 | °C | |
| HeatDeflectionTemperature5(0.45MPa,Unannealed,64.0mmSpan) | ***75-2/Bf | 116 | °C | ||
| 载荷下热变形温度(1.8MPa,未退火,3.20mm) | ASTMD648 | 85.0 | °C | ||
| 维卡软化温度 | ASTMD15256 | 86.7 | °C | ||
| ***306/A50 | 131 | °C | |||
| 线形热膨胀系数-流动(-40到40°C) | ASTME831 | 1.6E-4 | cm/cm/°C | ||
| 线形热膨胀系数-横向(-40到40°C) | ASTME831 | 9.7E-5 | cm/cm/°C |
未经改性的（PPO）树脂具有良好的力学性能、电性能、耐热性、阻燃性以及化学稳定性等，但是它的耐溶剂性差、制品容易发生应力开裂、缺口冲击强度低，另外它存在一个致命的弱点——熔体粘度高，加工成型性极差，纯PPO树脂不能采用注射方法成型，这样大大限制了它的应用。
为了克服这些缺点，或赋予其新的性能，人们对PPO进行了多种改性。其方法有化学（共聚、嵌段、接枝和网化等）和物理（共混、填充、增强和微发泡等）改性两种。