原包沙伯基础***高耐热PPO/PA NORYL GTX626
| 比重 | 1.09 | g/cm | ASTM D792 |
| 收缩率 - 流动(3.20 mm) | 1.3 到 1.4 | % | 内部方法 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 抗张强度1(屈服) | 62.1 | MPa | ASTM D638 |
| 伸长率2(断裂) | 83 | % | ASTM D638 |
| 弯曲模量3(100 mm 跨距) | 2280 | MPa | ASTM D790 |
| 弯曲强度4(屈服, 100 mm 跨距) | 95.8 | MPa | ASTM D790 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 悬壁梁缺口冲击强度 | ASTM D256 | ||
| -30°C | 120 | J/m | ASTM D256 |
| 23°C | 340 | J/m | ASTM D256 |
| 装有测量仪表的落镖冲击 | ASTM D3763 | ||
| -30°C, Energy at Peak Load | 36.6 | J | ASTM D3763 |
| 23°C, Energy at Peak Load | 31.2 | J | ASTM D3763 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 载荷下热变形温度(0.45 MPa, 未退火, 6.40 mm) | 179 | °C | ASTM D648 |
| RTI Elec | 50.0 | °C | UL 746 |
| RTI Imp | 50.0 | °C | UL 746 |
| RTI | 50.0 | °C | UL 746 |
| 可燃性 | 额定值 | 测试方法 | |
|---|---|---|---|
| UL 阻燃等级(1.50 mm) | HB | UL 94 |