PROPERTIES |
| TYPICAL VALUES | UNITS | TEST METHODS |
---|
MECHANICAL | 1) |
|
|
|
---|
Tensile Stress, yield, 5 mm/min |
| 25 | MPa | *** 527 |
---|
Tensile Strain, yield, 5 mm/min |
| 2.1 | % | *** 527 |
---|
Tensile Modulus, 1 mm/min |
| 3400 | MPa | *** 527 |
---|
Flexural Stress, yield, 2 mm/min |
| 49 | MPa | *** 178 |
---|
Flexural Stress, break, 2 mm/min |
| 39 | MPa | *** 178 |
---|
Flexural Strain, break, 2 mm/min |
| 5.9 | % | *** 178 |
---|
Flexural Modulus, 2 mm/min |
| 3900 | MPa | *** 178 |
---|
IMPACT | 1) |
|
|
|
---|
Izod Impact, unnotched 80*10*4 +23°C |
| 15 | kJ/m² | *** 180/1U |
---|
Izod Impact, notched 80*10*4 +23°C |
| 5 | kJ/m² | *** 180/1A |
---|
THERMAL | 1) |
|
|
|
---|
CTE, 23°C to 60°C, flow |
| 6.9E-05 | 1/°C | *** 11359-2 |
---|
CTE, 23°C to 60°C, xflow |
| 9.3E-05 | 1/°C | *** 11359-2 |
---|
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm |
| 95 | °C | *** 75/Bf |
---|
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm |
| 81 | °C | *** 75/Af |
---|
PHYSICAL | 1) |
|
|
|
---|
Mold Shrinkage, flow | 3) | 0.5 | % | SABIC method |
---|
Density |
| 1.38 | g/cm³ | *** 1183 |
---|
Water Absorption, (23°C/24hrs) |
| 0.24 | % | *** 62-1 |
---|
INJECTION MOLDING | 2) |
|
|
|
---|
Drying Temperature |
| 80 | °C |
|
---|
Drying Time |
| 4 | Hrs |
|
---|
Maximum Moisture Content |
| 0.05-0.1 | % |
|
---|
Melt Temperature |
| 260 | °C |
|
---|
Front - Zone 3 Temperature |
| 265-275 | °C |
|
---|
Middle - Zone 2 Temperature |
| 230-245 | °C |
|
---|
Rear - Zone 1 Temperature |
| 205-215 | °C |
|
---|
Mold Temperature |
| 70-80 | °C |
|
---|
Back Pressure |
| 0.2-0.3 | MPa |
|
---|
Screw Speed |
| 30-60 | rpm |
|
---|