LNP THERMOCOMP D351 玻璃纤维、阻燃剂
¥98.00
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
---|---|---|---|---|
FLAME CHARACTERISTICS | 1) | |||
UL Yellow Card Link | E207780-102099701 | - | - | |
Glow Wire Ignitability Temperature, 0.6 mm | 850 | °C | IEC 60695-2-13 | |
Glow Wire Ignitability Temperature, 1.5 mm | 875 | °C | IEC 60695-2-13 | |
Glow Wire Ignitability Temperature, 3.0 mm | 875 | °C | IEC 60695-2-13 | |
Glow Wire Flammability Index, 0.6 mm | 960 | °C | IEC 60695-2-12 | |
Glow Wire Flammability Index, 1.5 mm | 960 | °C | IEC 60695-2-12 | |
Glow Wire Flammability Index, 3.0 mm | 960 | °C | IEC 60695-2-12 | |
UL Recognized, 94V-0 Flame Class Rating | ≥0.6 | mm | UL 94 | |
UL Recognized, 94V-1 Flame Class Rating | ≥0.4 | mm | UL 94 | |
UL Recognized, 94V-2 Flame Class Rating | ≥0.3 | mm | UL 94 | |
MECHANICAL | 2) | |||
Tensile Stress, brk, Type I, 5 mm/min | 110 | MPa | ASTM D638 | |
Tensile Strain, brk, Type I, 5 mm/min | 2.7 | % | ASTM D638 | |
Tensile Modulus, 5 mm/min | 6680 | MPa | ASTM D638 | |
Flexural Stress, brk, 1.3 mm/min, 50 mm span | 167 | MPa | ASTM D790 | |
Flexural Modulus, 1.3 mm/min, 50 mm span | 6150 | MPa | ASTM D790 | |
Tensile Stress, break, 5 mm/min | 112 | MPa | *** 527 | |
Tensile Strain, break, 5 mm/min | 2.6 | % | *** 527 | |
Tensile Modulus, 1 mm/min | 6800 | MPa | *** 527 | |
Flexural Stress, break, 2 mm/min | 165 | MPa | *** 178 | |
Flexural Modulus, 2 mm/min | 6240 | MPa | *** 178 | |
IMPACT | 2) | |||
Izod Impact, notched 80*10*4 +23°C | 13 | kJ/m² | *** 180/1A | |
Izod Impact, notched 80*10*4 -30°C | 9 | kJ/m² | *** 180/1A | |
Izod Impact, notched 80*10*3 +23°C | 13 | kJ/m² | *** 180/1A | |
Izod Impact, notched 80*10*3 -30°C | 9 | kJ/m² | *** 180/1A | |
Izod Impact, unnotched 80*10*4 +23°C | 48 | kJ/m² | *** 180/1U | |
Izod Impact, unnotched 80*10*4 -30°C | 56 | kJ/m² | *** 180/1U | |
Izod Impact, unnotched 80*10*3 +23°C | 48 | kJ/m² | *** 180/1U | |
Izod Impact, unnotched 80*10*3 -30°C | 54 | kJ/m² | *** 180/1U | |
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 15 | kJ/m² | *** 179/1eA | |
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 10 | kJ/m² | *** 179/1eA | |
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 14 | kJ/m² | *** 179/1eA | |
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm | 55 | kJ/m² | *** 179/1eU | |
Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm | 67 | kJ/m² | *** 179/1eU | |
Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 59 | kJ/m² | *** 179/1eU | |
Izod Impact, unnotched, 23°C | 715 | J/m | ASTM D4812 | |
Izod Impact, notched, 23°C | 150 | J/m | ASTM D256 | |
Instrumented Dart Impact Energy @ peak, 23°C | 21 | J | ASTM D3763 | |
THERMAL | 2) | |||
HDT, 0.45 MPa, 3.2 mm, unannealed | 121 | °C | ASTM D648 | |
HDT, 1.82 MPa, 3.2mm, unannealed | 116 | °C | ASTM D648 | |
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 121 | °C | *** 75/Bf | |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 117 | °C | *** 75/Af | |
Vicat Softening Temp, Rate A/50 | 131 | °C | *** 306 | |
Vicat Softening Temp, Rate B/50 | 123 | °C | *** 306 | |
Vicat Softening Temp, Rate B/120 | 125 | °C | *** 306 | |
CTE, 23°C to 80°C, flow | 2.6E-05 | 1/°C | *** 11359-2 | |
CTE, 23°C to 80°C, xflow | 7.3E-05 | 1/°C | *** 11359-2 | |
Relative Temp Index, Elec | 1) | 80 | °C | UL 746B |
Relative Temp Index, Mech w/impact | 1) | 80 | °C | UL 746B |
Relative Temp Index, Mech w/o impact | 1) | 80 | °C | UL 746B |
PHYSICAL | 2) | |||
Density | 1.35 | g/cm³ | ASTM D792 | |
Mold Shrinkage, flow, 24 hrs | 4) | 0.2-0.4 | % | ASTM D955 |
Mold Shrinkage, xflow, 24 hrs | 4) | 0.2-0.4 | % | ASTM D955 |
Melt Flow Rate, 300°C/1.2 kgf | 12 | g/10 min | ASTM D1238 | |
Melt Flow Rate, 300°C/2.16 kgf | 24 | g/10 min | ASTM D1238 | |
Water Absorption, (23°C/saturated) | 0.07 | % | *** 62-1 | |
Moisture Absorption (23°C / 50% RH) | 0.03 | % | *** 62 | |
Melt Volume Rate, MVR at 300°C/1.2 kg | 10 | cm³/10 min | *** 1133 | |
Melt Volume Rate, MVR at 300°C/2.16 kg | 20 | cm³/10 min | *** 1133 | |
ELECTRICAL | 2) | |||
High Amp Arc Ignition (HAI), PLC 0 | ≥0.6 | mm | UL 746A | |
Comparative Tracking Index (UL) {PLC} | 3 | PLC Code | UL 746A | |
High Voltage Arc Track Rate {PLC} | 0 | PLC Code | UL 746A | |
Hot-Wire Ignition (HWI), PLC 0 | ≥0.6 | mm | UL 746A | |
Comparative Tracking Index | 200 | V | IEC 60112 | |
Dielectric Strength, in oil, 1.0 mm | 40 | kV/mm | IEC 60243-1 | |
Volume Resistivity | 1E16-1E17 | Ω.cm | IEC 62631-3-1 | |
Arc Resistance, Tungsten {PLC} | 7 | PLC Code | ASTM D495 | |
Dielectric Constant, 1.1 GHz | 3.24 | - | SABIC method | |
Dielectric Constant, 1.9 GHz | 3.28 | - | SABIC method | |
Dielectric Constant, 5 GHz | 3.28 | - | SABIC method | |
Dielectric Constant, 10 GHz | 3.27 | - | SABIC method | |
Dissipation Factor, 1.1 GHz | 0.0067 | - | SABIC method | |
Dissipation Factor, 1.9 GHz | 0.0066 | - | SABIC method | |
Dissipation Factor, 5 GHz | 0.007 | - | SABIC method | |
Dissipation Factor, 10 GHz | 0.0072 | - | SABIC method | |
INJECTION MOLDING | 3) | |||
Drying Temperature | 110 | °C | ||
Drying Time | 3-6 | Hrs | ||
Maximum Moisture Content | 0.02 | % | ||
Melt Temperature | 285-310 | °C | ||
Nozzle Temperature | 285-305 | °C | ||
Front - Zone 3 Temperature | 280-300 | °C | ||
Middle - Zone 2 Temperature | 270-290 | °C | ||
Rear - Zone 1 Temperature | 260-280 | °C | ||
Mold Temperature | 80-110 | °C | ||
Back Pressure | 0.1-0.3 | MPa | ||
Screw Speed | 50-90 | rpm |