ULTEM 4002 聚四氟乙烯填充,标准流量聚醚酰胺
¥98.00
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
---|---|---|---|---|
FLAME CHARACTERISTICS | 1) | |||
UL Yellow Card Link | E121562-502535 | - | - | |
UL Yellow Card Link 2 | E121562-100732300 | - | - | |
UL Recognized, 94-5VA Flame Class Rating | ≥1.9 | mm | UL 94 | |
UL Recognized, 94V-0 Flame Class Rating | ≥0.41 | mm | UL 94 | |
UV-light, water exposure/immersion | F1 | - | UL 746C | |
Glow Wire Flammability Index 960°C, passes at | 2) | 3.2 | mm | IEC 60695-2-12 |
Oxygen Index (LOI) | 46 | % | ISO 4589 | |
MECHANICAL | ||||
Taber Abrasion, CS-17, 1 kg | 15 | mg/1000cy | SABIC method | |
Tensile Stress, break, 5 mm/min | 115 | MPa | ISO 527 | |
Tensile Strain, break, 5 mm/min | 4 | % | ISO 527 | |
Tensile Modulus, 1 mm/min | 4500 | MPa | ISO 527 | |
Flexural Stress, break, 2 mm/min | 185 | MPa | ISO 178 | |
Flexural Modulus, 2 mm/min | 4500 | MPa | ISO 178 | |
Ball Indentation Hardness, H358/30 | 140 | MPa | ISO 2039-1 | |
IMPACT | ||||
Izod Impact, unnotched 80*10*4 +23°C | 30 | kJ/m² | ISO 180/1U | |
Izod Impact, unnotched 80*10*4 -30°C | 30 | kJ/m² | ISO 180/1U | |
Charpy Impact, notched, 23°C | 7 | kJ/m² | ISO 179/2C | |
THERMAL | ||||
Thermal Conductivity | 0.24 | W/m-°C | ISO 8302 | |
CTE, 23°C to 150°C, flow | 3.0E-05 | 1/°C | ISO 11359-2 | |
CTE, 23°C to 150°C, xflow | 5.1E-05 | 1/°C | ISO 11359-2 | |
Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 | |
Vicat Softening Temp, Rate A/50 | 223 | °C | ISO 306 | |
Vicat Softening Temp, Rate B/50 | 212 | °C | ISO 306 | |
Vicat Softening Temp, Rate B/120 | 217 | °C | ISO 306 | |
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 210 | °C | ISO 75/Be | |
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 205 | °C | ISO 75/Ae | |
Relative Temp Index, Elec | 1) | 170 | °C | UL 746B |
Relative Temp Index, Mech w/impact | 1) | 170 | °C | UL 746B |
Relative Temp Index, Mech w/o impact | 1) | 170 | °C | UL 746B |
PHYSICAL | ||||
Mold Shrinkage on Tensile Bar, flow | 0.4-0.6 | % | SABIC method | |
Density | 1.34 | g/cm³ | ISO 1183 | |
Water Absorption, (23°C/saturated) | 1 | % | ISO 62-1 | |
Moisture Absorption (23°C / 50% RH) | 0.6 | % | ISO 62 | |
Melt Volume Rate, MVR at 360°C/5.0 kg | 9 | cm³/10 min | ISO 1133 | |
ELECTRICAL | ||||
Volume Resistivity | 1.E+15 | Ω.cm | IEC 60093 | |
Surface Resistivity, ROA | >1.E+15 | Ω | IEC 60093 | |
Dielectric Strength, in oil, 0.8 mm | 34 | kV/mm | IEC 60243-1 | |
Dielectric Strength, in oil, 1.6 mm | 27 | kV/mm | IEC 60243-1 | |
Dielectric Strength, in oil, 3.2 mm | 15 | kV/mm | IEC 60243-1 | |
Relative Permittivity, 1 MHz | 2.9 | - | IEC 60250 | |
Dissipation Factor, 50/60 Hz | 0.0009 | - | IEC 60250 | |
Dissipation Factor, 1 MHz | 0.0025 | - | IEC 60250 | |
Dissipation Factor, 2450 MHz | 0.0046 | - | IEC 60250 | |
Comparative Tracking Index | 2) | 150 | V | IEC 60112 |
Comparative Tracking Index, M | 2) | 100 | V | IEC 60112 |
Relative Permittivity, 50/60 Hz | 3 | - | IEC 60250 | |
Comparative Tracking Index (UL) {PLC} | 4 | PLC Code | UL 746A | |
Hot-Wire Ignition (HWI), PLC 1 | ≥3 | mm | UL 746A | |
Hot-Wire Ignition (HWI), PLC 2 | ≥1.5 | mm | UL 746A | |
High Amp Arc Ignition (HAI), PLC 3 | ≥1.5 | mm | UL 746A | |
High Amp Arc Ignition (HAI), PLC 4 | ≥3 | mm | UL 746A | |
High Voltage Arc Track Rate {PLC} | 2 | PLC Code | UL 746A | |
Arc Resistance, Tungsten {PLC} | 6 | PLC Code | ASTM D495 | |
INJECTION MOLDING | ||||
Drying Temperature | 150 | °C | ||
Drying Time | 4-6 | Hrs | ||
Maximum Moisture Content | 0.02 | % | ||
Melt Temperature | 370-410 | °C | ||
Nozzle Temperature | 350-405 | °C | ||
Front - Zone 3 Temperature | 360-415 | °C | ||
Middle - Zone 2 Temperature | 350-405 | °C | ||
Rear - Zone 1 Temperature | 340-395 | °C | ||
Hopper Temperature | 80-120 | °C | ||
Mold Temperature | 140-180 | °C |