产品详情
PROPERTIES |
| TYPICAL VALUES | UNITS | TEST METHODS |
---|
FLAME CHARACTERISTICS | 1) |
|
|
|
---|
UL Yellow Card Link |
| E121562-221099 | - | - |
---|
UL Yellow Card Link 2 |
| E121562-470961 | - | - |
---|
UL Recognized, 94-5VA Flame Class Rating |
| ≥1.2 | mm | UL 94 |
---|
UL Recognized, 94V-0 Flame Class Rating |
| ≥0.25 | mm | UL 94 |
---|
Glow Wire Ignitability Temperature, 2.0 mm |
| 900 | °C | IEC 60695-2-13 |
---|
Glow Wire Flammability Index, 2.0 mm |
| 960 | °C | IEC 60695-2-12 |
---|
UV-light, water exposure/immersion |
| F1 | - | UL 746C |
---|
Oxygen Index (LOI) |
| 48 | % | ISO 4589 |
---|
INJECTION MOLDING | 2) |
|
|
|
---|
Drying Temperature |
| 150 | °C |
|
---|
Drying Time |
| 4-6 | Hrs |
|
---|
Drying Time (Cumulative) |
| 24 | Hrs |
|
---|
Maximum Moisture Content |
| 0.02 | % |
|
---|
Melt Temperature |
| 350-410 | °C |
|
---|
Nozzle Temperature |
| 345-410 | °C |
|
---|
Front - Zone 3 Temperature |
| 345-420 | °C |
|
---|
Middle - Zone 2 Temperature |
| 340-410 | °C |
|
---|
Rear - Zone 1 Temperature |
| 330-400 | °C |
|
---|
Hopper Temperature |
| 80-120 | °C |
|
---|
Mold Temperature |
| 135-180 | °C |
|
---|
Shot to Cylinder Size |
| 40-60 | % |
|
---|
Vent Depth |
| 0.025-0.076 | mm |
|
---|
Screw speed (Circumferential speed) |
| 0.15-0.25 | m/s |
|
---|
Screw Speed |
| 40-70 | rpm |
|
---|
Back Pressure |
| 0.3-1.5 | MPa |
|
---|
ELECTRICAL | 3) |
|
|
|
---|
Volume Resistivity |
| 1.E+15 | Ω.cm | IEC 60093 |
---|
Surface Resistivity, ROA |
| >1.E+15 | Ω | IEC 60093 |
---|
Dielectric Strength, in oil, 0.8 mm |
| 35 | kV/mm | IEC 60243-1 |
---|
Dielectric Strength, in oil, 1.6 mm |
| 26 | kV/mm | IEC 60243-1 |
---|
Dielectric Strength, in oil, 3.2 mm |
| 15 | kV/mm | IEC 60243-1 |
---|
Relative Permittivity, 50/60 Hz |
| 3.3 | - | IEC 60250 |
---|
Relative Permittivity, 1 MHz |
| 3.4 | - | IEC 60250 |
---|
Dissipation Factor, 50/60 Hz |
| 0.0016 | - | IEC 60250 |
---|
Dissipation Factor, 1 MHz |
| 0.0023 | - | IEC 60250 |
---|
Dielectric Constant | 6) |
|
|
|
---|
at 1.1 GHz |
| 3.51 | - | - |
at 5 GHz |
| 3.59 | - | - |
at 10 GHz |
| 3.60 | - | - |
Dissipation Factor | 6) |
|
|
|
---|
at 1.1 GHz |
| 0.0029 | - | - |
at 5 GHz |
| 0.0036 | - | - |
at 10 GHz |
| 0.0046 | - | - |
Comparative Tracking Index | 4) | 150 | V | IEC 60112 |
---|
Comparative Tracking Index, M | 4) | 100 | V | IEC 60112 |
---|
Volume Resistivity |
| 3.E+16 | Ω.cm | ASTM D257 |
---|
Dielectric Strength, in air, 1.6 mm |
| 24.8 | kV/mm | ASTM D149 |
---|
Dielectric Strength, in oil, 1.6 mm |
| 30.3 | kV/mm | ASTM D149 |
---|
Relative Permittivity, 1 kHz |
| 3.7 | - | ASTM D150 |
---|
Dissipation Factor, 1 kHz |
| 0.0015 | - | ASTM D150 |
---|
Comparative Tracking Index (UL) {PLC} | 1) | 4 | PLC Code | UL 746A |
---|
Hot-Wire Ignition (HWI), PLC 1 | 1) | ≥3 | mm | UL 746A |
---|
Hot-Wire Ignition (HWI), PLC 3 | 1) | ≥1.5 | mm | UL 746A |
---|
High Amp Arc Ignition (HAI), PLC 3 | 1) | ≥1.5 | mm | UL 746A |
---|
High Amp Arc Ignition (HAI), PLC 4 | 1) | ≥3 | mm | UL 746A |
---|
High Voltage Arc Track Rate {PLC} | 1) | 3 | PLC Code | UL 746A |
---|
Arc Resistance, Tungsten {PLC} | 1) | 6 | PLC Code | ASTM D495 |
---|
PHYSICAL | 3) |
|
|
|
---|
Density |
| 1.51 | g/cm³ | ISO 1183 |
---|
Moisture Absorption, (23°C/50% RH/24hrs) |
| 0.1 | % | ISO 62-4 |
---|
Moisture Absorption, (23°C/50% RH/Equilibrium) |
| 0.6 | % | ISO 62-4 |
---|
Water Absorption, (23°C/24hrs) |
| 0.16 | % | ISO 62-1 |
---|
Water Absorption, (23°C/saturated) |
| 0.9 | % | ISO 62-1 |
---|
Melt Volume Rate, MVR at 360°C/5.0 kg |
| 8 | cm³/10 min | ISO 1133 |
---|
Specific Gravity |
| 1.51 | - | ASTM D792 |
---|
Water Absorption, (23°C/24hrs) |
| 0.16 | % | ASTM D570 |
---|
Water Absorption, (23°C/Saturated) |
| 0.9 | % | ASTM D570 |
---|
Melt Flow Rate, 337°C/6.6 kgf |
| 7.6 | g/10 min | ASTM D1238 |
---|
Mold Shrinkage, flow, 3.2 mm | 5) | 0.2-0.4 | % | SABIC method |
---|
THERMAL | 3) |
|
|
|
---|
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm |
| 215 | °C | ISO 75/Bf |
---|
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm |
| 210 | °C | ISO 75/Af |
---|
Vicat Softening Temp, Rate A/50 |
| 225 | °C | ISO 306 |
---|
Vicat Softening Temp, Rate B/120 |
| 220 | °C | ISO 306 |
---|
Vicat Softening Temp, Rate B/50 |
| 213 | °C | ISO 306 |
---|
CTE, -40°C to 150°C, flow |
| 1.8E-05 | 1/°C | ISO 11359-2 |
---|
CTE, -40°C to 150°C, xflow |
| 4.8E-05 | 1/°C | ISO 11359-2 |
---|
Thermal Conductivity |
| 0.31 | W/m-°C | ISO 8302 |
---|
Ball Pressure Test, 125°C +/- 2°C |
| PASS | - | IEC 60695-10-2 |
---|
HDT, 0.45 MPa, 3.2 mm, unannealed |
| 215 | °C | ASTM D648 |
---|
HDT, 0.45 MPa, 6.4 mm, unannealed |
| 212 | °C | ASTM D648 |
---|
HDT, 1.82 MPa, 3.2mm, unannealed |
| 211 | °C | ASTM D648 |
---|
HDT, 1.82 MPa, 6.4 mm, unannealed |
| 210 | °C | ASTM D648 |
---|
CTE, -20°C to 150°C, flow |
| 1.8E-05 | 1/°C | ASTM E831 |
---|
CTE, -20°C to 150°C, xflow |
| 4.8E-05 | 1/°C | ASTM E831 |
---|
Relative Temp Index, Elec | 1) | 180 | °C | UL 746B |
---|
Relative Temp Index, Mech w/impact | 1) | 170 | °C | UL 746B |
---|
Relative Temp Index, Mech w/o impact | 1) | 180 | °C | UL 746B |
---|
IMPACT | 3) |
|
|
|
---|
Izod Impact, notched 80*10*4 +23°C |
| 10 | kJ/m² | ISO 180/1A |
---|
Izod Impact, notched 80*10*4 -30°C |
| 10 | kJ/m² | ISO 180/1A |
---|
Izod Impact, unnotched 80*10*4 +23°C |
| 40 | kJ/m² | ISO 180/1U |
---|
Izod Impact, unnotched 80*10*4 -30°C |
| 40 | kJ/m² | ISO 180/1U |
---|
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm |
| 10 | kJ/m² | ISO 179/1eA |
---|
Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm |
| 10 | kJ/m² | ISO 179/1eA |
---|
Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm |
| 40 | kJ/m² | ISO 179/1eU |
---|
Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm |
| 40 | kJ/m² | ISO 179/1eU |
---|
Izod Impact, notched, 23°C |
| 90 | J/m | ASTM D256 |
---|
Izod Impact, notched, -30°C |
| 80 | J/m | ASTM D256 |
---|
Izod Impact, Reverse Notched, 3.2 mm |
| 470 | J/m | ASTM D256 |
---|
Izod Impact, unnotched, 23°C |
| 600 | J/m | ASTM D4812 |
---|
Izod Impact, unnotched, -30°C |
| 600 | J/m | ASTM D4812 |
---|
MECHANICAL | 3) |
|
|
|
---|
Tensile Stress, break, 5 mm/min |
| 175 | MPa | ISO 527 |
---|
Tensile Strain, break, 5 mm/min |
| 2.4 | % | ISO 527 |
---|
Tensile Modulus, 1 mm/min |
| 10500 | MPa | ISO 527 |
---|
Flexural Stress, break, 2 mm/min |
| 240 | MPa | ISO 178 |
---|
Flexural Modulus, 2 mm/min |
| 9600 | MPa | ISO 178 |
---|
Ball Indentation Hardness, H358/30 |
| 165 | MPa | ISO 2039-1 |
---|
Taber Abrasion, CS-17, 1 kg |
| 20 | mg/1000cy | SABIC method |
---|
Hardness, Rockwell M |
| 110 | - | ISO 2039-2 |
---|
Tensile Stress, brk, Type I, 5 mm/min |
| 175 | MPa | ASTM D638 |
---|
Tensile Strain, brk, Type I, 5 mm/min |
| 2.5 | % | ASTM D638 |
---|
Tensile Modulus, 5 mm/min |
| 10400 | MPa | ASTM D638 |
---|
Flexural Stress, brk, 2.6 mm/min, 100 mm span |
| 230 | MPa | ASTM D790 |
---|
Flexural Modulus, 2.6 mm/min, 100 mm span |
| 9400 | MPa | ASTM D790 |
---|
Flexural Stress, brk, 1.3 mm/min, 50 mm span |
| 250 | MPa | ASTM D790 |
---|
Flexural Modulus, 1.3 mm/min, 50 mm span |
| 9700 | MPa | ASTM D790 |
---|
Hardness, Rockwell M |
| 114 | - | ASTM D785 |
---|
产品参数
- 否
- 中国
- 2300FC
- 注塑
- ULTEM 2300FC 30%玻璃纤维增强的标准流动无定形聚醚酰亚胺