PROPERTIES		TYPICAL VALUES	UNITS	TEST METHODS
FLAME CHARACTERISTICS	¹⁾
UL Yellow Card Link		E121562-221117	-	-
UL Recognized, 94-5VA Flame Class Rating		≥1.5	mm	UL 94
UL Recognized, 94V-0 Flame Class Rating		≥1.5	mm	UL 94
MECHANICAL
Tensile Stress, yld, Type I, 5 mm/min		117	MPa	ASTM D638
Tensile Stress, brk, Type I, 5 mm/min		112	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min		4	%	ASTM D638
Tensile Modulus, 5 mm/min		4750	MPa	ASTM D638
Flexural Stress, yld, 2.6 mm/min, 100 mm span		193	MPa	ASTM D790
Flexural Modulus, 2.6 mm/min, 100 mm span		4890	MPa	ASTM D790
IMPACT
Izod Impact, notched, 23°C		37	J/m	ASTM D256
Izod Impact, Reverse Notched, 3.2 mm		357	J/m	ASTM D256
THERMAL
HDT, 1.82 MPa, 6.4 mm, unannealed		215	°C	ASTM D648
Relative Temp Index, Elec	¹⁾	105	°C	UL 746B
Relative Temp Index, Mech w/impact	¹⁾	105	°C	UL 746B
Relative Temp Index, Mech w/o impact	¹⁾	105	°C	UL 746B
PHYSICAL
Specific Gravity		1.36	-	ASTM D792
Mold Shrinkage, flow, 3.2 mm		0.7-0.9	%	SABIC method
Mold Shrinkage, xflow, 3.2 mm		0.6-0.8	%	SABIC method
Melt Flow Rate, 337°C/6.6 kgf		6.9	g/10 min	ASTM D1238
ELECTRICAL
Comparative Tracking Index (UL) {PLC}		4	PLC Code	UL 746A
Hot-Wire Ignition (HWI), PLC 0		≥3	mm	UL 746A
Hot-Wire Ignition (HWI), PLC 1		≥1.5	mm	UL 746A
High Amp Arc Ignition (HAI), PLC 3		≥1.5	mm	UL 746A
High Amp Arc Ignition (HAI), PLC 4		≥3	mm	UL 746A
High Voltage Arc Track Rate {PLC}		3	PLC Code	UL 746A
Arc Resistance, Tungsten {PLC}		5	PLC Code	ASTM D495
INJECTION MOLDING
Drying Temperature		150	°C
Drying Time		4-6	Hrs
Drying Time (Cumulative)		24	Hrs
Maximum Moisture Content		0.02	%
Melt Temperature		365-390	°C
Nozzle Temperature		360-380	°C
Front - Zone 3 Temperature		365-390	°C
Middle - Zone 2 Temperature		355-375	°C
Rear - Zone 1 Temperature		345-365	°C
Mold Temperature		135-165	°C
Back Pressure		0.3-0.7	MPa
Screw Speed		40-70	rpm
Shot to Cylinder Size		40-60	%
Vent Depth		0.025-0.076	mm

为您推荐

ULTEM DU242 增强低温冲击，高流动性聚醚酰亚胺 ¥128.00
ULTEM EXUM0167 延展性提高，透明，标准流动聚醚酰胺 ¥128.00
ULTEM HU1100 用于医疗器械和制药应用。医疗保健管理的变革 ¥128.00
ULTEM HU1110 增强流动性聚醚酰亚胺 ¥288.00
ULTEM HU2100 10%玻璃纤维填充，标准流量聚醚酰亚胺 ¥128.00
ULTEM HU2110 10%玻璃纤维填充，增强流动性聚醚酰亚胺 ¥128.00

供应商网> 特种塑料> ULTEM CRS5111 10%玻璃纤维填充的增流聚醚酰胺

在线问

产品参数

是否进口否
厂家(产地)中国
牌号CRS5111
用途级别注塑

1/2

¥180.00 在线咨询

进店客服获取最低报价拨打电话

ULTEM CRS5111 10%玻璃纤维填充的增流聚醚酰胺: ¥180.00