PROPERTIES |
| TYPICAL VALUES | UNITS | TEST METHODS |
---|
FLAME CHARACTERISTICS | 1) |
|
|
|
---|
UL Yellow Card Link |
| E121562-100737020 | - | - |
---|
UL Recognized, 94V-0 Flame Class Rating |
| ≥0.75 | mm | UL 94 |
---|
Oxygen Index (LOI) |
| 46 | % | ASTM D2863 |
---|
NBS Smoke Density, Flaming, Ds 4 min |
| 0.7 | - | ASTM E662 |
---|
MECHANICAL |
|
|
|
|
---|
Tensile Stress, yld, Type I, 5 mm/min |
| 95 | MPa | ASTM D638 |
---|
Tensile Stress, brk, Type I, 5 mm/min |
| 90 | MPa | ASTM D638 |
---|
Tensile Strain, yld, Type I, 5 mm/min |
| 7 | % | ASTM D638 |
---|
Tensile Strain, brk, Type I, 5 mm/min |
| 85 | % | ASTM D638 |
---|
Tensile Modulus, 5 mm/min |
| 2900 | MPa | ASTM D638 |
---|
Flexural Stress, yld, 1.3 mm/min, 50 mm span |
| 140 | MPa | ASTM D790 |
---|
Flexural Modulus, 1.3 mm/min, 50 mm span |
| 3000 | MPa | ASTM D790 |
---|
Tensile Stress, yield, 50 mm/min |
| 97 | MPa | ISO 527 |
---|
Tensile Stress, break, 50 mm/min |
| 80 | MPa | ISO 527 |
---|
Tensile Strain, yield, 50 mm/min |
| 7 | % | ISO 527 |
---|
Tensile Strain, break, 50 mm/min |
| 80 | % | ISO 527 |
---|
Flexural Stress, yield, 2 mm/min |
| 136 | MPa | ISO 178 |
---|
Flexural Modulus, 2 mm/min |
| 2800 | MPa | ISO 178 |
---|
IMPACT |
|
|
|
|
---|
Izod Impact, notched, 23°C |
| 70 | J/m | ASTM D256 |
---|
Izod Impact, Reverse Notched, 3.2 mm |
| 3300 | J/m | ASTM D256 |
---|
Instrumented Dart Impact Total Energy, 23°C |
| 93 | J | ASTM D3763 |
---|
Instrumented Impact Total Energy, 0°C |
| 99 | J | ASTM D3763 |
---|
Instrumented Impact Total Energy, -20°C |
| 93 | J | ASTM D3763 |
---|
Instrumented Dart Impact Ductility, 23°C |
| 100 | % | ASTM D3763 |
---|
Instrumented Dart Impact Ductility, 0°C |
| 100 | % | ASTM D3763 |
---|
Instrumented Dart Impact Ductility, -20°C |
| 90 | % | ASTM D3763 |
---|
Izod Impact, unnotched 80*10*4 +23°C |
| NB | kJ/m² | ISO 180/1U |
---|
Izod Impact, unnotched 80*10*4 -30°C |
| NB | kJ/m² | ISO 180/1U |
---|
Izod Impact, notched 80*10*4 +23°C |
| 6 | kJ/m² | ISO 180/1A |
---|
Izod Impact, notched 80*10*4 -30°C |
| 6 | kJ/m² | ISO 180/1A |
---|
Charpy Impact, notched, 23°C |
| 11 | kJ/m² | ISO 179/2C |
---|
THERMAL |
|
|
|
|
---|
HDT, 0.45 MPa, 6.4 mm, unannealed |
| 214 | °C | ASTM D648 |
---|
HDT, 1.82 MPa, 6.4 mm, unannealed |
| 204 | °C | ASTM D648 |
---|
CTE, -20°C to 150°C, flow |
| 5.6E-05 | 1/°C | ASTM E831 |
---|
CTE, -20°C to 150°C, xflow |
| 5.5E-05 | 1/°C | ASTM E831 |
---|
Thermal Conductivity |
| 0.19 | W/m-°C | ASTM C177 |
---|
CTE, 23°C to 150°C, flow |
| 5.E-05 | 1/°C | ISO 11359-2 |
---|
CTE, 23°C to 150°C, xflow |
| 5.E-05 | 1/°C | ISO 11359-2 |
---|
Vicat Softening Temp, Rate A/50 |
| 219 | °C | ISO 306 |
---|
Vicat Softening Temp, Rate B/50 |
| 212 | °C | ISO 306 |
---|
Vicat Softening Temp, Rate B/120 |
| 212 | °C | ISO 306 |
---|
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm |
| 205 | °C | ISO 75/Be |
---|
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm |
| 190 | °C | ISO 75/Ae |
---|
Relative Temp Index, Elec | 1) | 105 | °C | UL 746B |
---|
Relative Temp Index, Mech w/impact | 1) | 105 | °C | UL 746B |
---|
Relative Temp Index, Mech w/o impact | 1) | 105 | °C | UL 746B |
---|
PHYSICAL |
|
|
|
|
---|
Specific Gravity |
| 1.28 | - | ASTM D792 |
---|
Mold Shrinkage, flow, 3.2 mm |
| 0.5-0.7 | % | SABIC method |
---|
Melt Flow Rate, 337°C/6.6 kgf |
| 10 | g/10 min | ASTM D1238 |
---|
Density |
| 1.28 | g/cm³ | ISO 1183 |
---|
Melt Volume Rate, MVR at 360°C/5.0 kg |
| 14 | cm³/10 min | ISO 1133 |
---|
ELECTRICAL |
|
|
|
|
---|
Comparative Tracking Index (UL) {PLC} |
| 4 | PLC Code | UL 746A |
---|
Hot-Wire Ignition (HWI), PLC 1 |
| ≥1.5 | mm | UL 746A |
---|
Hot-Wire Ignition (HWI), PLC 2 |
| ≥0.75 | mm | UL 746A |
---|
High Amp Arc Ignition (HAI), PLC 1 |
| ≥0.75 | mm | UL 746A |
---|
INJECTION MOLDING |
|
|
|
|
---|
Drying Temperature |
| 150 | °C |
|
---|
Drying Time |
| 6-8 | Hrs |
|
---|
Drying Time (Cumulative) |
| 24 | Hrs |
|
---|
Maximum Moisture Content |
| 0.02 | % |
|
---|
Melt Temperature |
| 355-390 | °C |
|
---|
Nozzle Temperature |
| 345-390 | °C |
|
---|
Front - Zone 3 Temperature |
| 345-390 | °C |
|
---|
Middle - Zone 2 Temperature |
| 335-390 | °C |
|
---|
Rear - Zone 1 Temperature |
| 330-390 | °C |
|
---|
Mold Temperature |
| 130-160 | °C |
|
---|
Back Pressure |
| 0.3-0.7 | MPa |
|
---|
Screw Speed |
| 40-70 | rpm |
|
---|
Shot to Cylinder Size |
| 40-60 | % |
|
---|
Vent Depth |
| 0.025-0.076 | mm |
|
---|