Density / Specific Gravity | |||
-- | 1.11 | g/cm | ASTM D792 |
23°C | 1.11 | g/cm | *** 1183 |
Melt Mass-Flow Rate (MFR)(240°C/10.0 kg) | 24 | g/10 min | *** 1133 |
Molding Shrinkage | 0.20 to 0.40 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
Rockwell Hardness(R-Scale, 23°C) | 118 | ASTM D785,*** 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Strength | |||
-- | 78.0 | MPa | ASTM D638 |
23°C | 81.0 | MPa | *** 527-2 |
Tensile Elongation | |||
Break | 3.0 | % | ASTM D638 |
Break, 23°C | 3.0 | % | *** 527-2 |
Flexural Modulus | |||
-- | 4100 | MPa | ASTM D790 |
23°C | 4200 | MPa | *** 178 |
Flexural Strength | |||
-- | 120 | MPa | ASTM D790 |
23°C | 127 | MPa | *** 178 |
| Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength(23°C) | 9.0 | kJ/m | *** 179 |
Notched Izod Impact(23°C, 12.7 mm) | 83 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load | |||
1.8 MPa, Unannealed, 6.40 mm | 100 | °C | ASTM D648 |
1.8 MPa, Unannealed | 100 | °C | *** 75-2/A |
Vicat Softening Temperature | 95.0 | °C |