Density(23°C) | 1.20 | g/cm | ISO 1183 |
Apparent (Bulk) Density3 | 0.66 | g/cm | ISO 60 |
Melt Mass-Flow Rate (MFR)(300°C/1.2 kg) | 3.0 | g/10 min | ISO 1133 |
Melt Volume-Flow Rate (MVR)(300°C/1.2 kg) | 3.0 | cm/10min | ISO 1133 |
Tensile Modulus(23°C) | 2400 | MPa | ISO 527-2/1 |
Tensile Stress | ISO 527-2/50 | ||
Yield, 23°C | 67.0 | MPa | |
Break, 23°C | 65.0 | MPa | |
Tensile Strain | ISO 527-2/50 | ||
Yield, 23°C | 6.4 | % | |
Break, 23°C | 110 | % | |
Nominal Tensile Strain at Break(23°C) | > 50 | % | ISO 527-2/50 |
Flexural Modulus5(23°C) | 2400 | MPa | ISO 178 |
Flexural Stress5 | ISO 178 | ||
23°C | 98.0 | MPa | |
3.5% Strain, 23°C | 75.0 | MPa |
Charpy Notched Impact Strength7 | ISO 179/1eA | ||
-30°C, Complete Break | 14 | kJ/m | |
23°C, Partial Break | 70 | kJ/m |
Heat Deflection Temperature | |||
0.45 MPa, Unannealed | 139 | °C | ISO 75-2/B |
1.8 MPa, Unannealed | 127 | °C | ISO 75-2/A |
Glass Transition Temperature8 | 146 | °C | ISO 11357-2 |
Flame Rating(2.0 mm) | V-0 | UL 94 |