Density | 1.28 | g/cm³ | ISO 1183 |
Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 12 | g/10 min | ISO 1133 |
Molding Shrinkage - Flow | 0.40 to 0.60 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus | 4300 | MPa | ISO 527-1/1 |
Tensile Stress | ISO 527-2/5 | ||
Yield | 85.0 | MPa | |
Break | 50.0 | MPa | |
Tensile Strain (Break) | 10 | % | ISO 527-2/5 |
Flexural Modulus 3 | 4100 | MPa | ISO 178 |
Flexural Stress 3 | 139 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength (23°C) | 6.0 | kJ/m² | ISO 179/1eA |
Notched Izod Impact Strength (23°C) | 7.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load | |||
0.45 MPa, Unannealed | 141 | °C | ISO 75-2/B |
1.8 MPa, Unannealed | 137 | °C | ISO 75-2/A |
1.8 MPa, Annealed | 139 | °C | ISO 75-2/A |
Vicat Softening Temperature | 145 | °C | ISO 306/B50 |
Ball Indentation Temperature | > 130 | °C | IEC 60335-1 |
CLTE - Flow | 1.5E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
Electric Strength | 70 | kV/mm | IEC 60243-1 |