Grivory HT1V-6 FWA black 9225 is a Polyamide 6I/6T Copolymer (Nylon 6I/6T) material filled with 60% glass fiber.
Density | 1.78 | -- | g/cm | ISO 1183 |
Molding Shrinkage | ISO 294-4 | |||
Across Flow | 0.20 | -- | % | |
Flow | 0.10 | -- | % | |
Water Absorption | ISO 62 | |||
Saturation, 23°C | 3.0 | -- | % | |
Equilibrium, 23°C, 50% RH | 1.2 | -- | % | |
| Hardness | Dry | Conditioned | Unit | Test Method |
Ball Indentation Hardness | 360 | 360 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
Tensile Modulus | 23000 | 22500 | MPa | ISO 527-2 |
Tensile Stress(Break) | 260 | 250 | MPa | ISO 527-2 |
Tensile Strain(Break) | 1.5 | 1.5 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
Charpy Notched Impact Strength | ISO 179/1eA | |||
-30°C | 10 | 10 | kJ/m | |
23°C | 11 | 11 | kJ/m | |
Charpy Unnotched Impact Strength | ISO 179/1eU | |||
-30°C | 75 | 75 | kJ/m | |
23°C | 75 | 75 | kJ/m |
| Thermal | Dry | Conditioned | Unit | Test Method |
Heat Deflection Temperature | ||||
1.8 MPa, Unannealed | 290 | -- | °C | ISO 75-2/A |
8.0 MPa, Unannealed | 215 | -- | °C | ISO 75-2/C |
Continuous Use Temperature | ||||
--3 | 140 | -- | °C | ISO 2578 |
--4 | 270 | -- | °C | Internal Method |
Melting Temperature5 | 325 | -- | °C | ISO 11357-3 |
CLTE | ISO 11359-2 | |||
Flow | 1.5E-5 | -- | cm/cm/°C | |
Transverse | 4.0E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
Surface Resistivity | -- | 1.0E+12 | ohms | IEC 60093 |
Volume Resistivity | 1.0E+13 | 1.0E+13 | ohms·cm | IEC 60093 |
Electric Strength | 30 | 30 | kV/mm | IEC 60243-1 |
Comparative Tracking Index | -- | 600 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
Flammability Classification(0.8 mm) | HB | -- | IEC 60695-11-10, -20 |
PPA树脂是既有半结晶态的，也有非结晶态的，其玻璃化温度在255°F左右。非结晶态的PPA主要用于要求阻隔性能的场合；半结晶态的PPA树脂主要用于注塑加工，也用于其它熔融加工工艺下文主要介绍后者——半结晶态PPA树脂，特别注明的除外。半结晶态PPAS的熔点约590°F，以不透明矩形切片的形式供应。