| 物理性能 | 比重 | ASTMD792,ISO1183 | 1.10 | g/cm | |
| 熔流率（熔体流动速率）(200°C/3.8kg) | ASTMD1238 | 42 | g/10min | ||
| 溶化体积流率（MVR） | 280°C/1.2kg | ISO1133 | 20.0 | cm/10min | |
| 280°C/2.16kg | ISO1133 | 41.0 | cm/10min | ||
| 吸水率 | 饱和,23°C | ISO62 | 0.13 | % | |
| 平衡,23°C,50%RH | ISO62 | 0.020 | % | ||
| 机械性能 | --1 | ASTMD638 | 2200 | MPa | |
| -- | ISO527-2/1 | 2420 | MPa | ||
| 屈服2 | ASTMD638 | 54.0 | MPa | ||
| 屈服 | ISO527-2/50 | 55.0 | MPa | ||
| 断裂3 | ASTMD638 | 55.0 | MPa | ||
| 断裂 | ISO527-2/50 | 42.0 | MPa | ||
| 屈服4 | ASTMD638 | 3.0 | % | ||
| 屈服 | ISO527-2/50 | 3.0 | % | ||
| 断裂5 | ASTMD638 | 12 | % | ||
| 断裂 | ISO527-2/50 | 11 | % | ||
| 50.0mm跨距6 | ASTMD790 | 2400 | MPa | ||
| --7 | ISO178 | 2530 | MPa | ||
| --8 | ISO178 | 82.0 | MPa | ||
| 屈服,50.0mm跨距9 | ASTMD790 | 84.0 | MPa | ||
| 冲击性能 | 简支梁缺口冲击强度10(23°C) | ISO179/1eA | 6.0 | kJ/m | |
| 23°C | ASTMD256 | 78 | J/m | ||
| -30°C11 | ISO180/1A | 5.0 | kJ/m | ||
| 23°C12 | ISO180/1A | 6.0 | kJ/m | ||
| 热性能 | 1.8MPa,未退火,3.20mm | ASTMD648 | 80.0 | °C | |
| 1.8MPa,未退火,64.0mm跨距13 | ISO75-2/Af | 74.0 | °C | ||
| -- | ASTMD152514 | 105 | °C | ||
| ISO306/B50 | 91.0 | °C | |||
| ISO306/B120 | 93.0 | °C | |||
| 线形热膨胀系数 | 流动:-40到40°C | ASTME831,ISO11359-2 | 8.3E-5 | cm/cm/°C | |
| 横向:-40到40°C | ASTME831,ISO11359-2 | 8.0E-5 | cm/cm/°C | ||
| 可燃性 | UL阻燃等级 | 1.50mm,TestingbySABIC | UL94 | V-1 | |
| 2.50mm,TestingbySABIC | UL94 | V-0 |
PPO材料作为世界五大通用工程塑料之一，***，相对密度小，（PPO/PA同类产品也仅为1.10-1.13g/cm3），是五大通用工程塑料中密度***小的,具有良好的机械强度，抗蠕变性，耐应力松弛，抗疲劳强度高。