***沙伯基础***PPO/PA NORYL GTX6203矿物增强20%
Density / Specific Gravity | |||
-- | 1.25 | g/cm | ASTM D792 |
-- | 1.24 | g/cm | *** 1183 |
Melt Mass-Flow Rate (MFR)(280°C/5.0 kg) | 20 | g/10 min | ASTM D1238 |
Melt Volume-Flow Rate (MVR)(280°C/5.0 kg) | 20 | cm/10min | *** 1133 |
Molding Shrinkage | Internal Method | ||
Across Flow : 3.20 mm | 0.60 to 0.90 | % | |
Flow : 3.20 mm | 0.60 to 0.90 | % | |
Water Absorption | *** 62 | ||
Saturation, 23°C | 3.2 | % | |
Equilibrium, 23°C, 50% RH | 1.1 | % |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus | |||
--1 | 4600 | MPa | ASTM D638 |
-- | 4900 | MPa | *** 527-2/1 |
Charpy Notched Impact Strength6(23°C) | 5.0 | kJ/m | *** 179/1eA |
Notched Izod Impact | |||
-30°C | 50 | J/m | ASTM D256 |
23°C | 60 | J/m | ASTM D256 |
-30°C7 | 5.0 | kJ/m | *** 180/1A |
23°C7 | 6.0 | kJ/m | *** 180/1A |
Unnotched Izod Impact Strength7(23°C) | 50 | kJ/m | *** 180/1U |
Instrumented Dart Impact(23°C, Total Energy) | 10.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load | |||
0.45 MPa, Unannealed, 3.20 mm | 190 | °C | ASTM D648 |
0.45 MPa, Unannealed, 4.00 mm, 100 mm Span8 | 190 | °C | *** 75-2/Be |