塞拉尼斯OMNILON PA6 U GR50 BK2000 50%GF+PA6
ISO | Value | Unit | Test Standard |
Density | 1560 | kg/m | ISO 1183 |
Tensile modulus | 16300 | MPa | ISO 527-2/1A |
Tensile stress at break, 5mm/min | 185 | MPa | ISO 527-2/1A |
Tensile strain at break, 5mm/min | 1.6 | % | ISO 527-2/1A |
Charpy notched impact strength, 23°C | 13 | kJ/m | ISO 179/1eA |
DTUL at 1.8 MPa | 213 | °C | ISO 75-1, -2 |
DTUL at 0.45 MPa | 218 | °C | ISO 75-1, -2 |
Pre Drying | Value | Unit | Test Standard |
Necessary low maximum residual moisture content | 0.15 | % | - |
Drying time | 4 - 8 | h | - |
Drying temperature | 80 - 90 | °C | - |
Temperature | Value | Unit | Test Standard |
Zone1 temperature | 220 - 230 | °C | - |
Zone2 temperature | 225 - 235 | °C | - |
Zone3 temperature | 235 - 245 | °C | - |
Zone4 temperature | 245 - 255 | °C | - |
Nozzle temperature | 255 - 270 | °C | - |
Melt temperature | 250 - 270 | °C | - |
Mold temperature | 60 - 80 | °C | - |
Hot runner temperature | 255 - 270 | °C | - |
PA6日常用品中的应用
PA6玻纤增强材料具有良好的尺寸稳定性及低翘曲性、焊锡性及烤漆性、易喷涂、可过超声波焊接、材料光泽度好,可染成各种鲜艳的颜色,为了满足在工业品方面的使用要求,增强PA6材料应具备以下要求:
1). 强度和耐久性,优良的刚性和耐热性的结合
2). 优化部件设计,***的着色性能,***的表面外观,能够适用于复杂的结构成型,并帮助设计***开发新造型产品
3). 良好的加工性,***的流动性及热稳定性使材料加工条件更为宽松,使注塑件微型化
4). 极高的热稳定性,能在高达270度的波峰焊锡中不挂锡
5). ***的温度和频率范围内恒定的电气性,确保装置设备的使用***百安全