Density / Specific Gravity | 1.28 | g/cm³ | ASTM D792 |
Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 12 | g/10 min | ASTM D1238 |
Molding Shrinkage | |||
Flow | 0.35 to 0.50 | % | ASTM D955 |
Across Flow | 0.40 to 0.55 | % | ASTM D955 |
Flow | 0.40 to 0.60 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus 3 | 4000 | MPa | ASTM D638 |
Tensile Strength 4 | ASTM D638 | ||
Yield | 65.0 | MPa | |
Break | 65.0 | MPa | |
Tensile Elongation 4 (Break) | 4.0 | % | ASTM D638 |
Flexural Modulus 5 | 3800 | MPa | ASTM D790 |
Flexural Strength 5 | 120 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength (23°C) | 6.0 | kJ/m² | ISO 179/1eA |
Notched Izod Impact Strength 6 (23°C) | 9.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load | |||
0.45 MPa, Unannealed | 138 | °C | ASTM D648 |
0.45 MPa, Unannealed | 141 | °C | ISO 75-2/B |
1.8 MPa, Unannealed | 129 | °C | ASTM D648 |
1.8 MPa, Unannealed | 133 | °C | ISO 75-2/A |
1.8 MPa, Annealed | 139 | °C | ISO 75-2/A |
Vicat Softening Temperature | 145 | °C | ISO 306/B50 |
Ball Indentation Temperature | > 130 | °C | IEC 60335-1 |
CLTE - Flow | 1.5E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Unit | Test Method |
Flame Rating 7 | UL 94 | ||
1.5 mm | V-0 | ||
3.0 mm | 5V | ||
Glow Wire Flammability Index 7 (2.0 mm) | 960 | °C | IEC 60695-2-12 |