PROPERTIES |
| TYPICAL VALUES | UNITS | TEST METHODS |
---|
FLAME CHARACTERISTICS | 1) |
|
|
|
---|
UL Yellow Card Link |
| E207780-100801552 | - | - |
---|
UL Recognized, 94-5VB Flame Class Rating |
| ≥2.5 | mm | UL 94 |
---|
UL Recognized, 94V-0 Flame Class Rating |
| ≥1.5 | mm | UL 94 |
---|
UL Recognized, 94V-1 Flame Class Rating |
| ≥1.1 | mm | UL 94 |
---|
UL Recognized, 94HB Flame Class Rating |
| 0.4 | mm | UL 94 |
---|
INJECTION MOLDING | 2) |
|
|
|
---|
Drying Temperature |
| 80-90 | °C |
|
---|
Drying Time |
| 3-4 | Hrs |
|
---|
Drying Time (Cumulative) |
| 8 | Hrs |
|
---|
Maximum Moisture Content |
| 0.04 | % |
|
---|
Melt Temperature |
| 245-275 | °C |
|
---|
Nozzle Temperature |
| 245-275 | °C |
|
---|
Front - Zone 3 Temperature |
| 245-275 | °C |
|
---|
Middle - Zone 2 Temperature |
| 220-265 | °C |
|
---|
Rear - Zone 1 Temperature |
| 220-255 | °C |
|
---|
Mold Temperature |
| 60-80 | °C |
|
---|
Back Pressure |
| 0.3-0.7 | MPa |
|
---|
Screw Speed |
| 40-70 | rpm |
|
---|
Shot to Cylinder Size |
| 30-80 | % |
|
---|
Vent Depth |
| 0.038-0.076 | mm |
|
---|
MECHANICAL | 3) |
|
|
|
---|
Tensile Stress, yld, Type I, 50 mm/min |
| 63 | MPa | ASTM D638 |
---|
Tensile Stress, brk, Type I, 50 mm/min |
| 42 | MPa | ASTM D638 |
---|
Tensile Strain, yld, Type I, 50 mm/min |
| 4 | % | ASTM D638 |
---|
Tensile Strain, brk, Type I, 50 mm/min |
| 65 | % | ASTM D638 |
---|
Tensile Modulus, 50 mm/min |
| 2480 | MPa | ASTM D638 |
---|
Flexural Strength, 1.3 mm/min, 50 mm span |
| 89 | MPa | ASTM D790 |
---|
Flexural Modulus, 1.3 mm/min, 50 mm span |
| 2240 | MPa | ASTM D790 |
---|
Tensile Stress, yield, 50 mm/min |
| 67 | MPa | ISO 527 |
---|
Tensile Stress, break, 50 mm/min |
| 44 | MPa | ISO 527 |
---|
Tensile Strain, yield, 50 mm/min |
| 4.2 | % | ISO 527 |
---|
Tensile Strain, break, 50 mm/min |
| 56 | % | ISO 527 |
---|
Tensile Modulus, 1 mm/min |
| 2500 | MPa | ISO 527 |
---|
Flexural Strength, 2 mm/min |
| 95 | MPa | ISO 178 |
---|
Flexural Modulus, 2 mm/min |
| 2500 | MPa | ISO 178 |
---|
Flexural Stress at 3.5% strain, 2 mm/min |
| 82 | MPa | ISO 178 |
---|
IMPACT | 3) |
|
|
|
---|
Izod Impact, notched, 23°C |
| 550 | J/m | ASTM D256 |
---|
Izod Impact, notched 80*10*4 +23°C |
| 6.7 | kJ/m² | ISO 180/1A |
---|
Izod Impact, unnotched 80*10*4 +23°C |
| 137 | kJ/m² | ISO 180/1U |
---|
Instrumented Dart Impact Total Energy, 23°C |
| 65 | J | ASTM D3763 |
---|
Multi-Axial Instrumented Impact Energy @ peak, 23°C |
| 91 | J | ISO 6603-2 |
---|
Multi-Axial Instrumented Impact Total Energy, 23°C |
| 124 | J | ISO 6603-2 |
---|
THERMAL | 3) |
|
|
|
---|
HDT, 1.82 MPa, 3.2mm, unannealed |
| 78 | °C | ASTM D648 |
---|
HDT 1.8 MPa, 80*10*4mm, Cut |
| 82 | °C | ISO 75-1&2 |
---|
Vicat Softening Temp, Rate B/50 |
| 102 | °C | ASTM D1525 |
---|
PHYSICAL | 3) |
|
|
|
---|
Specific Gravity |
| 1.2 | - | ASTM D792 |
---|
Melt Flow Rate, 266°C/5.0 kgf |
| 26 | g/10 min | ASTM D1238 |
---|
Mold Shrinkage, flow, 3.2 mm | 4) | 0.5-0.8 | % | SABIC method |
---|
ELECTRICAL | 3) |
|
|
|
---|
Dielectric Constant, 1.1 GHz |
| 2.85 | - | SABIC method |
---|
Dielectric Constant, 1.9 GHz |
| 2.86 | - | SABIC method |
---|
Dielectric Constant, 5 GHz |
| 2.81 | - | SABIC method |
---|
Dielectric Constant, 10 GHz |
| 2.817 | - | SABIC method |
---|
Dissipation Factor, 1.1 GHz |
| 0.00696 | - | SABIC method |
---|
Dissipation Factor, 1.9 GHz |
| 0.00676 | - | SABIC method |
---|
Dissipation Factor, 5 GHz |
| 0.00817 | - | SABIC method |
---|
Dissipation Factor, 10 GHz |
| 0.00778 | - | SABIC method |
---|