盛禧奥EMERGE PC 8230-8耐候阻燃高耐热
Density / Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 8.0 | g/10 min | ASTM D1238 |
Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955, ISO 294-4 |
Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus 3 | 2300 | MPa | ASTM D638 |
Tensile Strength 4 | ASTM D638 | ||
Yield | 60.0 | MPa | |
Break | 65.0 | MPa | |
Tensile Elongation 4 | ASTM D638 | ||
Yield | 6.0 | % | |
Break | 120 | % | |
Flexural Modulus 5 | 2400 | MPa | ASTM D790 |
Flexural Strength 5 | 90.0 | MPa | ASTM D790 |
Impact | Nominal Value | Unit | Test Method |
Notched Izod Impact | ASTM D256 | ||
-40°C | 600 | J/m | |
-30°C | 650 | J/m | |
23°C | 750 | J/m |
Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load (1.8 MPa, Unannealed) | 125 | °C | ASTM D648 |
Vicat Softening Temperature | 145 | °C | ASTM D1525 6 |
Ball Indentation Temperature | > 125 | °C | IEC 60335-1 |
CLTE - Flow (-40 to 80°C) | 6.5E-5 | cm/cm/°C | ASTM D696 |
Electrical | Nominal Value | Unit | Test Method |
Arc Resistance | PLC 7 | ASTM D495 | |
Flammability | Nominal Value | Unit | Test Method |
Flame Rating 7 | UL 94 | ||
1.5 mm | V-0 | ||
3.0 mm |
|