Density / Specific Gravity | 1.20 | g/cm³ | ASTM D792, ISO 1183 |
Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 31 | g/10 min | ASTM D1238, ISO 1133 |
Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955, ISO 294-4 |
Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus | |||
-- 3 | 2300 | MPa | ASTM D638 |
-- | 2400 | MPa | ISO 527-1/1 |
Tensile Strength | |||
Yield 4 | 60.0 | MPa | ASTM D638 |
Yield | 60.0 | MPa | ISO 527-2/50 |
Break 4 | 65.0 | MPa | ASTM D638 |
Break | 67.0 | MPa | ISO 527-2/50 |
Charpy Notched Impact Strength (23°C) | 15 | kJ/m² | ISO 179/1eA |
Notched Izod Impact | |||
23°C | 400 | J/m | ASTM D256 |
23°C | 55 | kJ/m² | ISO 180/1A |
Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load | |||
0.45 MPa, Annealed | 141 | °C | ISO 75-2/B |
1.8 MPa, Unannealed | 123 | °C | ASTM D648 |
1.8 MPa, Unannealed | 122 | °C | ISO 75-2/A |
1.8 MPa, Annealed | 136 | °C | ISO 75-2/A |
Vicat Softening Temperature | 141 | °C | ISO 306/B50 |
Ball Indentation Temperature | > 125 | °C | IEC 60335-1 |
CLTE - Flow | |||
-40 to 80°C | 6.5E-5 | cm/cm/°C | ASTM D696 |
-- | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
Electrical | Nominal Value | Unit | Test Method |
Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
Electric Strength | 17 | kV/mm | IEC 60243-1 |
Dissipation Factor | IEC 60250 | ||
50 Hz | 1.0E-3 | ||
1 MHz | 2.0E-3 | ||
Comparative Tracking Index (2.00 mm, Solution A) | 225 | V | IEC 60112 |
Flammability | Nominal Value | Unit | Test Method |
Flame Rating 7 | UL 94 | ||
0.75 mm | V-2 | ||
1.5 mm | V-2 | ||
2.0 mm | V-2 | ||
3.0 mm | V-0 |