Density / Specific Gravity | 1.20 | g/cm³ | ASTM D792, ISO 1183 |
Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 10 | g/10 min | ASTM D1238, ISO 1133 |
Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955, ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
Rockwell Hardness (R-Scale) | 123 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus | |||
-- 3 | 2300 | MPa | ASTM D638 |
-- | 2200 | MPa | ISO 527-1/1 |
Tensile Strength | |||
Yield 4 | 60.0 | MPa | ASTM D638 |
Yield | 60.0 | MPa | ISO 527-2/50 |
Break 4 | 65.0 | MPa | ASTM D638 |
Break | 58.0 | MPa | ISO 527-2/50 |
Notched Izod Impact | |||
23°C | 750 | J/m | ASTM D256 |
23°C | 10 | kJ/m² | ISO 180/1A |
Instrumented Dart Impact 7 (23°C, Total Energy) | 58.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load | |||
0.45 MPa, Unannealed | 139 | °C | ISO 75-2/B |
1.8 MPa, Unannealed | 126 | °C | ASTM D648 |
1.8 MPa, Unannealed | 125 | °C | ISO 75-2/A |
Vicat Softening Temperature | |||
-- | 149 | °C | ASTM D1525 8 |
-- | 144 | °C | ISO 306/B50 |
-- | 150 | °C | ISO 306/A120 |