盛禧奥EMERGE PC 8410-22透明防火
Density / Specific Gravity | 1.20 | g/cm³ | ASTM D792, ISO 1183 |
Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 22 | g/10 min | ASTM D1238, ISO 1133 |
Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955, ISO 294-4 |
Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus | |||
-- 3 | 2300 | MPa | ASTM D638 |
-- | 2400 | MPa | ISO 527-1/1 |
Tensile Strength | |||
Yield 4 | 60.0 | MPa | ASTM D638 |
Yield | 60.0 | MPa | ISO 527-2/50 |
Break 4 | 65.0 | MPa | ASTM D638 |
Break | 70.0 | MPa | ISO 527-2/50 |
Charpy Notched Impact Strength (23°C) | 20 | kJ/m² | ISO 179/1eA |
Notched Izod Impact | |||
23°C | 600 | J/m | ASTM D256 |
23°C | 60 | kJ/m² | ISO 180/1A |
Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load | |||
0.45 MPa, Annealed | 142 | °C | ISO 75-2/B |
1.8 MPa, Unannealed | 124 | °C | ASTM D648 |
1.8 MPa, Unannealed | 122 | °C | ISO 75-2/A |
1.8 MPa, Annealed | 139 | °C | ISO 75-2/A |
Vicat Softening Temperature | 147 | °C | ISO 306/B50 |