VALOX ENH8530 非溴化阻燃剂PBT/PET的UL等级为V0
参数
  • 否是否进口
  • 中国厂家(产地)
  • ENH8530 牌号
广东 东莞 不限
东莞市聚浩塑化有限公司 2年
进入店铺 在线咨询
产品详情

PROPERTIES
TYPICAL VALUESUNITSTEST METHODS
FLAME CHARACTERISTICS1)


UL Yellow Card Link
E45329-100700420--
UL Recognized, 94-5VA Flame Class Rating
≥2mmUL 94
UL Recognized, 94V-0 Flame Class Rating
≥1.5mmUL 94
Glow Wire Ignitability Temperature, 3.0 mm
800°CIEC 60695-2-13
Glow Wire Ignitability Temperature, 1.5 mm
750°CIEC 60695-2-13
Glow Wire Ignitability Temperature, 0.8 mm
750°CIEC 60695-2-13
Glow Wire Flammability Index, 3.0 mm
960°CIEC 60695-2-12
Glow Wire Flammability Index, 1.5 mm
850°CIEC 60695-2-12
Glow Wire Flammability Index, 0.8 mm
960°CIEC 60695-2-12
MECHANICAL2)


Tensile Stress, yld, Type I, 5 mm/min
75MPaASTM D638
Tensile Stress, brk, Type I, 5 mm/min
75MPaASTM D638
Tensile Strain, yld, Type I, 5 mm/min
2%ASTM D638
Tensile Strain, brk, Type I, 5 mm/min
2%ASTM D638
Tensile Modulus, 5 mm/min
7200MPaASTM D638
Flexural Stress, yld, 1.3 mm/min, 50 mm span
110MPaASTM D790
Flexural Stress, brk, 1.3 mm/min, 50 mm span
110MPaASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span
6000MPaASTM D790
Tensile Stress, yield, 5 mm/min
75MPaISO 527
Tensile Stress, break, 5 mm/min
75MPaISO 527
Tensile Strain, yield, 5 mm/min
2%ISO 527
Tensile Strain, break, 5 mm/min
2%ISO 527
Tensile Modulus, 1 mm/min
7400MPaISO 527
Flexural Stress, yield, 2 mm/min
125MPaISO 178
Flexural Stress, break, 2 mm/min
125MPaISO 178
Flexural Strain, break, 2 mm/min
3%ISO 178
Flexural Modulus, 2 mm/min
6300MPaISO 178
Ball Indentation Hardness, H358/30
142MPaISO 2039-1
Hardness, Rockwell R
120-ISO 2039-2
IMPACT2)


Charpy Impact, unnotched, 23°C
23kJ/m²ISO 179/2C
Charpy Impact, unnotched, -30°C
20kJ/m²ISO 179/2C
Izod Impact, unnotched, 23°C
330J/mASTM D4812
Izod Impact, unnotched, -30°C
280J/mASTM D4812
Izod Impact, notched, 23°C
45J/mASTM D256
Izod Impact, notched, 0°C
45J/mASTM D256
Izod Impact, notched, -30°C
45J/mASTM D256
Izod Impact, unnotched 80*10*4 +23°C
22kJ/m²ISO 180/1U
Izod Impact, unnotched 80*10*4 -30°C
20kJ/m²ISO 180/1U
Izod Impact, notched 80*10*4 +23°C
5kJ/m²ISO 180/1A
Izod Impact, notched 80*10*4 0°C
5kJ/m²ISO 180/1A
Izod Impact, notched 80*10*4 -30°C
5kJ/m²ISO 180/1A
Charpy Impact, notched, 23°C
5kJ/m²ISO 179/2C
Charpy Impact, notched, -30°C
5kJ/m²ISO 179/2C
THERMAL2)


Vicat Softening Temp, Rate A/50
220°CASTM D1525
Vicat Softening Temp, Rate B/50
202°CASTM D1525
HDT, 0.45 MPa, 3.2 mm, unannealed
215°CASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed
190°CASTM D648
CTE, -40°C to 40°C, flow
3.1E-051/°CISO 11359-2
CTE, -40°C to 40°C, xflow
6.3E-051/°CISO 11359-2
CTE, 23°C to 150°C, flow
4.6E-051/°CISO 11359-2
CTE, 23°C to 150°C, xflow
1.65E-041/°CISO 11359-2
Ball Pressure Test, 125°C +/- 2°C
PASSES-IEC 60695-10-2
Vicat Softening Temp, Rate A/50
215°CISO 306
Vicat Softening Temp, Rate B/50
196°CISO 306
Vicat Softening Temp, Rate B/120
200°CISO 306
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm
215°CISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm
180°CISO 75/Af
Relative Temp Index, Elec1)130°CUL 746B
Relative Temp Index, Mech w/impact1)75°CUL 746B
Relative Temp Index, Mech w/o impact1)130°CUL 746B
PHYSICAL2)


Specific Gravity
1.46-ASTM D792
Filler Content
15%ASTM D229
Melt Flow Rate, 265°C/2.16kgf
20g/10 minASTM D1238
Melt Volume Rate, MVR at 250°C/5 kg
11cm³/10 minASTM D1238
Density
1.46g/cm³ISO 1183
Melt Flow Rate, 250°C/5.0 kg
15g/10 minISO 1133
Melt Volume Rate, MVR at 265°C/1.2 kg
5cm³/10 minISO 1133
Melt Volume Rate, MVR at 265°C/2.16 kg
13cm³/10 minISO 1133
Melt Volume Rate, MVR at 265°C/5.0 kg
45cm³/10 minISO 1133
Melt Viscosity, 260°C, 1500 sec-1
145Pa-sISO 11443
ELECTRICAL2)


Volume Resistivity
1.E+15Ω.cmASTM D257
Dielectric Strength, in oil, 0.8 mm
38kV/mmASTM D149
Dielectric Strength, in oil, 1.6 mm
28kV/mmASTM D149
Dielectric Strength, in oil, 3.2 mm
19kV/mmASTM D149
Relative Permittivity, 1 MHz
3.3-ASTM D150
Dissipation Factor, 1 MHz
0.01-ASTM D150
Volume Resistivity
1.E+15Ω.cmIEC 60093
Surface Resistivity, ROA
>1.E+15ΩIEC 60093
Dielectric Strength, in oil, 0.8 mm
38kV/mmIEC 60243-1
Dielectric Strength, in oil, 1.6 mm
28kV/mmIEC 60243-1
Dielectric Strength, in oil, 3.2 mm
19kV/mmIEC 60243-1
Relative Permittivity, 1 MHz
3.3-IEC 60250
Dissipation Factor, 1 MHz
0.01-IEC 60250
Comparative Tracking Index4)400VIEC 60112
Comparative Tracking Index (UL) {PLC}
1PLC CodeUL 746A
Hot-Wire Ignition (HWI), PLC 0
≥1.5mmUL 746A
Hot-Wire Ignition (HWI), PLC 3
≥0.8mmUL 746A
High Amp Arc Ignition (HAI), PLC 0
≥0.8mmUL 746A
INJECTION MOLDING3)


Drying Temperature
110-120°C
Drying Time
4-6Hrs
Maximum Moisture Content
0.02%
Melt Temperature
260-285°C
Nozzle Temperature
265-275°C
Front - Zone 3 Temperature
260-280°C
Middle - Zone 2 Temperature
255-280°C
Rear - Zone 1 Temperature
240-260°C
Hopper Temperature
40-60°C
Mold Temperature
60-110°C


为您推荐
供应商网> 特种塑料> VALOX ENH8530 非溴化阻燃剂PBT/PET的UL等级为V0
    在线问
    产品参数
    1/2
    ¥98.00 在线咨询
    进店 客服 获取最低报价 拨打电话
    VALOX ENH8530 非溴化阻燃剂PBT/PET的UL等级为V0
    ¥98.00
    • 采购产品
    • 采购数量
    • 联系电话
    《服务条款》 并允许推荐更多供应商为您服务
    请阅读并同意《服务条款》

    获取成功

    请您注意近期来电

    看这里，您也可以拨打电话咨询产品哦~

    咨询电话：𐃇𐃈𐃇 𐃉𐃊𐃋𐃋 𐃌𐃋𐃌𐃈

    关闭 产品推荐
    知道了