| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
|---|---|---|---|---|
| MECHANICAL | 1) | |||
| Tensile Stress, break | 270 | MPa | ASTM D638 | |
| Tensile Strain, break | 1.6 | % | ASTM D638 | |
| Tensile Modulus, 50 mm/min | 19650 | MPa | ASTM D638 | |
| Flexural Stress | 430 | MPa | ASTM D790 | |
| Flexural Modulus | 18020 | MPa | ASTM D790 | |
| Tensile Stress, break | 261 | MPa | ISO 527 | |
| Tensile Strain, break | 1.6 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 23280 | MPa | ISO 527 | |
| Flexural Stress | 433 | MPa | ISO 178 | |
| Flexural Modulus | 18920 | MPa | ISO 178 | |
| IMPACT | 1) | |||
| Izod Impact, notched, 23°C | 412 | J/m | ASTM D256 | |
| Instrumented Dart Impact Energy @ peak, 23°C | 18 | J | ASTM D3763 | |
| Multiaxial Impact | 18 | J | ISO 6603 | |
| Izod Impact, unnotched 80*10*4 +23°C | 102 | kJ/m² | ISO 180/1U | |
| Izod Impact, notched 80*10*4 +23°C | 54 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 -40°C | 43 | kJ/m² | ISO 180/1A | |
| THERMAL | 1) | |||
| HDT, 1.82 MPa, 3.2mm, unannealed | 247 | °C | ASTM D648 | |
| CTE, -40°C to 40°C, flow | 1.76E-05 | 1/°C | ASTM E831 | |
| CTE, -40°C to 40°C, xflow | 5.36E-05 | 1/°C | ASTM E831 | |
| CTE, -40°C to 40°C, flow | 1.7E-05 | 1/°C | ISO 11359-2 | |
| CTE, -40°C to 40°C, xflow | 5.3E-05 | 1/°C | ISO 11359-2 | |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 252 | °C | ISO 75/Bf | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 252 | °C | ISO 75/Af | |
| PHYSICAL | 1) | |||
| Density | 1.71 | g/cm³ | ASTM D792 | |
| Moisture Absorption, (23°C/50% RH/24 hrs) | 0.44 | % | ASTM D570 | |
| Mold Shrinkage, flow, 24 hrs | 0.2 | % | ASTM D955 | |
| Mold Shrinkage, xflow, 24 hrs | 0.4 | % | ASTM D955 | |
| Mold Shrinkage, flow, 24 hrs | 0.2 | % | ISO 294 | |
| Mold Shrinkage, xflow, 24 hrs | 0.4 | % | ISO 294 | |
| Density | 1.71 | g/cm³ | ISO 1183 | |
| INJECTION MOLDING | 2) | |||
| Drying Temperature | 80 | °C | ||
| Drying Time | 4 | Hrs | ||
| Maximum Moisture Content | 0.15-0.25 | % | ||
| Melt Temperature | 290-305 | °C | ||
| Front - Zone 3 Temperature | 290-300 | °C | ||
| Middle - Zone 2 Temperature | 290-300 | °C | ||
| Rear - Zone 1 Temperature | 280-295 | °C | ||
| Mold Temperature | 95-110 | °C | ||
| Back Pressure | 0.2-0.3 | MPa | ||
| Screw Speed | 30-60 | rpm |
为您推荐
-
VALOX ENH4550 25%玻璃纤维增强的注塑 ¥98.00
-
-
VALOX ENH4565 33%的玻璃纤维增强、抗热震 ¥98.00
-
-
-
VALOX ENH8560 玻纤填充 ¥98.00
-
LNP STAT-KON Compound VC108. ¥98.00
-
LNP STAT-KON Compound VC112 ¥117.00
-
LNP STAT-KON Compound VC120 ¥78.00
-
LNP STAT-KON Compound VC130 ¥18.00
-
-
-
Xenoy IQNH2900 UL94 V-0无溴阻燃 ¥118.00
-
ULTEM 1000 无定形透明聚醚酰亚胺（PEI）塑料 ¥98.00
-
-
-
ULTEM 1100F ¥128.00
-
ULTEM 2100 10%玻璃纤维填充，标准流量聚醚酰亚胺 ¥128.00
在线问
产品参数
- 否
- 中国
- RX06424
- 注塑