PROPERTIES |
| TYPICAL VALUES | UNITS | TEST METHODS |
---|
FLAME CHARACTERISTICS | 1) |
|
|
|
---|
UL Yellow Card Link |
| E45329-103390789 | - | - |
---|
UL Recognized, 94V-0 Flame Class Rating |
| ≥0.75 | mm | UL 94 |
---|
UL Recognized, 94-5VB Flame Class Rating |
| ≥3 | mm | UL 94 |
---|
Glow Wire Ignitability Temperature, 3.0 mm |
| 775 | °C | IEC 60695-2-13 |
---|
Glow Wire Ignitability Temperature, 1.5 mm |
| 750 | °C | IEC 60695-2-13 |
---|
Glow Wire Ignitability Temperature, 0.75 mm |
| 775 | °C | IEC 60695-2-13 |
---|
Glow Wire Flammability Index, 3.0 mm |
| 960 | °C | IEC 60695-2-12 |
---|
Glow Wire Flammability Index, 1.5 mm |
| 960 | °C | IEC 60695-2-12 |
---|
Glow Wire Flammability Index, 0.75 mm |
| 960 | °C | IEC 60695-2-12 |
---|
MECHANICAL | 2) |
|
|
|
---|
Tensile Stress, yld, Type I, 5 mm/min |
| 137 | MPa | ASTM D638 |
---|
Tensile Stress, brk, Type I, 5 mm/min |
| 137 | MPa | ASTM D638 |
---|
Tensile Strain, yld, Type I, 5 mm/min |
| 2.4 | % | ASTM D638 |
---|
Tensile Strain, brk, Type I, 5 mm/min |
| 2.4 | % | ASTM D638 |
---|
Tensile Modulus, 5 mm/min |
| 11600 | MPa | ASTM D638 |
---|
Flexural Stress, yld, 1.3 mm/min, 50 mm span |
| 180 | MPa | ASTM D790 |
---|
Flexural Modulus, 1.3 mm/min, 50 mm span |
| 9400 | MPa | ASTM D790 |
---|
Tensile Stress, yield, 5 mm/min |
| 140 | MPa | ISO 527 |
---|
Tensile Stress, break, 5 mm/min |
| 140 | MPa | ISO 527 |
---|
Tensile Strain, yield, 5 mm/min |
| 2.4 | % | ISO 527 |
---|
Tensile Strain, break, 5 mm/min |
| 2.4 | % | ISO 527 |
---|
Tensile Modulus, 1 mm/min |
| 11500 | MPa | ISO 527 |
---|
Flexural Stress, yield, 2 mm/min |
| 185 | MPa | ISO 178 |
---|
Flexural Modulus, 2 mm/min |
| 9400 | MPa | ISO 178 |
---|
IMPACT | 2) |
|
|
|
---|
Charpy Impact, unnotched, 23°C |
| 60 | kJ/m² | ISO 179/2C |
---|
Charpy Impact, unnotched, -30°C |
| 60 | kJ/m² | ISO 179/2C |
---|
Izod Impact, unnotched, 23°C |
| 800 | J/m | ASTM D4812 |
---|
Izod Impact, unnotched, -30°C |
| 600 | J/m | ASTM D4812 |
---|
Izod Impact, notched, 23°C |
| 80 | J/m | ASTM D256 |
---|
Izod Impact, notched, -30°C |
| 60 | J/m | ASTM D256 |
---|
Instrumented Dart Impact Total Energy, 23°C |
| 9 | J | ASTM D3763 |
---|
Izod Impact, notched 80*10*4 +23°C |
| 14 | kJ/m² | ISO 180/1A |
---|
Izod Impact, notched 80*10*4 -30°C |
| 14 | kJ/m² | ISO 180/1A |
---|
Charpy Impact, notched, 23°C |
| 12 | kJ/m² | ISO 179/2C |
---|
Charpy Impact, notched, -30°C |
| 12 | kJ/m² | ISO 179/2C |
---|
THERMAL | 2) |
|
|
|
---|
Vicat Softening Temp, Rate B/50 |
| 205 | °C | ASTM D1525 |
---|
HDT, 0.45 MPa, 3.2 mm, unannealed |
| 218 | °C | ASTM D648 |
---|
HDT, 1.82 MPa, 3.2mm, unannealed |
| 206 | °C | ASTM D648 |
---|
CTE, -40°C to 40°C, flow |
| 1.9E-05 | 1/°C | ASTM E831 |
---|
CTE, -40°C to 40°C, xflow |
| 7.E-05 | 1/°C | ASTM E831 |
---|
CTE, -40°C to 150°C, flow |
| 2.E-05 | 1/°C | ASTM E831 |
---|
CTE, -40°C to 150°C, xflow |
| 9.8E-05 | 1/°C | ASTM E831 |
---|
CTE, -40°C to 40°C, flow |
| 1.9E-05 | 1/°C | ISO 11359-2 |
---|
CTE, -40°C to 40°C, xflow |
| 7.E-05 | 1/°C | ISO 11359-2 |
---|
CTE, 23°C to 80°C, flow |
| 1.9E-05 | 1/°C | ISO 11359-2 |
---|
CTE, 23°C to 80°C, xflow |
| 8.E-05 | 1/°C | ISO 11359-2 |
---|
Ball Pressure Test, 125°C +/- 2°C |
| Pass | - | IEC 60695-10-2 |
---|
Relative Temp Index, Elec | 1) | 130 | °C | UL 746B |
---|
Relative Temp Index, Mech w/impact | 1) | 140 | °C | UL 746B |
---|
Relative Temp Index, Mech w/o impact | 1) | 140 | °C | UL 746B |
---|
PHYSICAL | 2) |
|
|
|
---|
Specific Gravity |
| 1.6 | - | ASTM D792 |
---|
Mold Shrinkage on Tensile Bar, flow | 4) | 0.1-0.4 | % | SABIC method |
---|
Mold Shrinkage, flow, 3.2 mm | 4) | 0.1-0.4 | % | SABIC method |
---|
Mold Shrinkage on Tensile Bar, xflow | 4) | 0.4-0.8 | % | SABIC method |
---|
Mold Shrinkage, xflow, 3.2 mm | 4) | 0.4-0.8 | % | SABIC method |
---|
Melt Flow Rate, 250°C/5.0 kgf |
| 24 | g/10 min | ASTM D1238 |
---|
Density |
| 1.61 | g/cm³ | ISO 1183 |
---|
Water Absorption, (23°C/saturated) |
| 0.23 | % | ISO 62-1 |
---|
Moisture Absorption (23°C / 50% RH) |
| 0.06 | % | ISO 62 |
---|
Melt Volume Rate, MVR at 250°C/5.0 kg |
| 18 | cm³/10 min | ISO 1133 |
---|
Melt Volume Rate, MVR at 265°C/5.0 kg |
| 20 | cm³/10 min | ISO 1133 |
---|
INJECTION MOLDING | 3) |
|
|
|
---|
Drying Temperature |
| 110-120 | °C |
|
---|
Drying Time |
| 2-4 | Hrs |
|
---|
Maximum Moisture Content |
| 0.02 | % |
|
---|
Melt Temperature |
| 245-260 | °C |
|
---|
Nozzle Temperature |
| 230-255 | °C |
|
---|
Front - Zone 3 Temperature |
| 240-260 | °C |
|
---|
Middle - Zone 2 Temperature |
| 235-250 | °C |
|
---|
Rear - Zone 1 Temperature |
| 230-240 | °C |
|
---|
Hopper Temperature |
| 40-60 | °C |
|
---|
Mold Temperature |
| 40-100 | °C |
|
---|
ELECTRICAL | 2) |
|
|
|
---|
Comparative Tracking Index (UL) {PLC} |
| 2 | PLC Code | UL 746A |
---|
Hot-Wire Ignition (HWI), PLC 0 |
| ≥0.75 | mm | UL 746A |
---|
High Amp Arc Ignition (HAI), PLC 0 |
| ≥0.75 | mm | UL 746A |
---|
High Voltage Arc Track Rate {PLC} |
| 0 | PLC Code | UL 746A |
---|
Arc Resistance, Tungsten {PLC} |
| 6 | PLC Code | ASTM D495 |
---|
产品参数
- 否
- 中国
- ENH4565
- 注塑
- VALOX ENH4565 33%的玻璃纤维增强、抗热震